Single-crystalline superalloy CMSX-4 is studied in the as-cast state and after heat treatment, with material being taken from turbine blade castings. The effect of the heat treatment on the defect structure of the root area near the selector/root connection is emphasized. Multiscale analysis is performed to correlate results obtained by X-ray topography and positron annihilation lifetime spectroscopy (PALS). Electron microscopy observations were also carried out to characterize the inhomogeneity in dendritic structure. The X-ray topography was used to compare defects of the misorientation nature, occurring in as-cast and treated states. The type and concentration of defects before and after heat treatment in different root areas were determined using the PALS method, which enables voids, mono-vacancies, and dislocations to be taken into account. In this way, differences in the concentration of defects caused by heat treatment are rationalized.

An analysis of the defects in the vicinity of the selector–root connection plane occurring during the creation of single-crystalline turbine blades made of CMSX-6 Ni-based superalloy was performed. X-ray diffraction topography, scanning electron microscopy, and positron annihilation lifetime spectroscopy were used. Comparing the area of undisturbed axial growth of dendrites to the area of lateral growth concluded that the low-angle boundaries-like (LAB-like) defects were created in the root as a result of unsteady-state lateral growth of some secondary dendrite arms in layers of the root located directly at the selector–root connection plane. Additional macroscopic low-angle boundaries (LABs) with higher misorientation angles were created as a result of concave curvatures of liquidus isotherm in platform-like regions near selector–root connections. Two kinds of vacancy-type defects, mono-vacancies and vacancy clusters, were determined in relation to the LABs and LAB-like defects. Only mono-vacancies appeared in the areas of undisturbed axial growth. Reasons for the creation of macroscopic LABs and LAB-like defects, and their relationships with vacancy-type defects were discussed.

In the work the single-crystalline alloy CMSX-4 was studied. The main aim of the study was an attempt to find correlations between images of X-Ray topography, X-ray diffraction maps of lattice parameter and misorientation angle and Scanning Electron Microscopy (SEM) images obtained by back-scattered electron (BSE) technique. Topography images were obtained by Auleytner method with wide beam. Diffractometer provided by EFG company was used for obtaining orientation and lattice parameter maps. Material for research was produced in Research and Development Laboratory for Aerospace Materials of Rzeszów University of Technology. Casts were obtained in ALD furnace by the Bridgman technique. It was found that X-ray topograms were correlated with SEM images of microstructures as well as with orientation and lattice parameter maps. X-Ray topograms showed high contrast bands which corresponded to dendrite arms. There was a correlation between low angle boundary and lattice parameter map.