Phosphogypsum (PG) is a major hazardous by-product of the phosphate industry. The whole world is facing the challenge of increasing stockpiles of PG, which significantly affect safety and the environment. Recycling this material may be an environmentally friendly and safe solution to this challenge. In this paper, we searched the Web of Science database for 2369 articles from 1975 to 2022 using “phosphogypsum” as the keyword. Using the VOSviewer as the literature visualisation tool, density visualisation was performed with keywords as the analysis units, and it was found that the researchers focused mainly on PG applications in construction and radionuclides. Over the years, different routes to PG valorisation have been developed in the agricultural, construction, environmental and energy sectors, and these topics are described in this review. As infrastructure projects, highway engineering is characterised by a large land area and high resource consumption. Therefore, applying PG to road materials can significantly increase the reuse and consumption of PG and reduce PG stockpiles. We hope that PG can be used for road construction on a large scale in the future. This paper focuses on the latest developments in PG as road materials. The most serious difficulty in using PG as road materials at present is that it contains radionuclides and heavy metal impurities, which can be purified by pretreatment methods. However, how to scale it up requires continuous research.

The advantages of asphalt pavement in terms of driving comfort, construction efficiency, and ease of maintenance have established it as the predominant choice for high-grade pavements at present. However, being highly sensitive to temperature and stress, asphalt performance is significantly influenced by external environmental conditions and loading, making it susceptible to various distress phenomena. Particularly in high-latitude regions, asphalt pavement cracking severely limits asphalt pavement’s functional performance and service lifespan under cold climatic conditions. To enhance the low-temperature cracking resistance of asphalt pavement in cold regions, tools such as VOS viewer 1.6.20 and Connected Papers were utilized to systematically organize, analyze, and summarize relevant research from the past 40 years. The results reveal that temperature shrinkage cracks and thermal fatigue cracks represent the primary forms of asphalt pavement distress in these regions. Cracking in asphalt pavement in cold regions is primarily influenced by structural design, pavement materials, construction technology, and climatic conditions. Among these factors, surface layer stiffness, base layer type, and the rate of temperature decrease exert the most significant impact on cracking resistance, collectively accounting for approximately 45.4% of all cracking-related factors. The low-temperature performance of asphalt pavement can be effectively improved through several strategies, including adopting full-thickness asphalt pavement with a skeleton-dense structure or reduced average particle size, incorporating functional layers, appropriately increasing the thickness of the upper layer and the compaction temperature of the lower layer, utilizing continuous surface layer construction techniques, and applying advanced materials. High-performance modifiers such as SBR and SBS, nanomaterials with good low-temperature performance, and warm mixing processes designed for cold regions have proven particularly effective. Among various improvement methods, asphalt modification has demonstrated superior effectiveness in enhancing the deformation capacity of asphalt and its mixtures, significantly boosting the low-temperature performance of asphalt pavements. Asphalt modification accounts for approximately 50% of the improvement methods evaluated in this study, with an average improvement in low-temperature performance reaching up to 143%. This paper provides valuable insights into the underlying causes of cracking distress in asphalt pavements in cold regions and offers essential guidance for improving the service quality of such pavements in these challenging environments.

Semi-flexible pavement material (SFPM) combines the advantages and avoids the disadvantages of asphalt concrete flexible pavement and cement concrete rigid pavement. However, due to the problem of interfacial strength of composite materials, SFPM is prone to cracking diseases, which limits the further application of SFPM. Hence, it is necessary to optimize the composition design of SFPM and improve its road performance. In this study, the effects of cationic emulsified asphalt, silane coupling agent and styrene–butadiene latex on the improvement of SFPM performance were compared and analyzed. The influence of modifier dosage and preparation parameters on the road performance of SFPM was investigated by an orthogonal experimental design combined with principal component analysis (PCA). The best modifier and the corresponding preparation process were selected. On this basis, the mechanism of SFPM road performance improvement was further analyzed by scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) spectral analysis. The results show that adding modifiers can significantly enhance the road performance of SFPM. Compared to silane coupling agents and styrene–butadiene latex, cationic emulsified asphalt changes the internal structure of cement-based grouting material and increases the interfacial modulus of SFPM by 242%, allowing cationic emulsified asphalt-SFPM (C-SFPM) to exhibit better road performance. According to the results of the principal component analysis, C-SFPM has the best overall performance compared to other SFPMs. Therefore, cationic emulsified asphalt is the most effective modifier for SFPM. The optimal amount of cationic emulsified asphalt is 5%, and the best preparation process involves vibration at a frequency of 60 Hz for 10 min and 28 days of maintenance. The study provides a method and basis for improving the road performance of SFPM and a reference for designing the material composition of SFPM mixes.

To improve the thermal-aging stability and rheological performance of styrene–butadiene rubber (SBR)-modified asphalt, phenolic resin (PF) was introduced in the process of preparing SBR-modified asphalt by melt blending. The effect of PF and SBR on the high and low-temperature rheological performance of the asphalt binder before and after aging was evaluated by a temperature and frequency sweep using a dynamic shear rheometer (DSR). Fourier transform infrared spectroscopy (FTIR), gel permeation chromatography (GPC), and fluorescence microscopy (FM) were used to further investigate the effect of PF and SBR on the thermal stability and morphological characteristics of the asphalt binder. The results showed that the addition of PF can enhance the high-temperature deformation resistance and short-term aging resistance of SBR-modified asphalt. Moreover, PF and SBR form an embedded network structure within the asphalt binder and alleviate the deterioration of the polymer during the aging process. Compared with SBR-modified asphalt, the chemical system of composite-modified asphalt is more stable, and it can remain stable with an aging time of less than 5 h.