Medulla tetrapanacis is composed of a lignocellulosic biopolymer and has a regular porous structure, which makes it a potential biomass material for preparing porous N-doped biochar. Herewith, N-doped Medulla tetrapanacis biochar (UBC) was successfully prepared by modification with urea and NaHCO₃ under pyrolysis at 700 °C. The nitrogen-containing groups were efficiently introduced into biochar, and the micro-pore structures of the UBC were developed with sizeable specific surface area, which was loaded with massive adsorption sites. The adsorption kinetics and isotherms of the UBC conformed to pseudo-second-order and Langmuir model. The superior adsorption capacities of the UBC for methylene blue (MB) and congo red (CR) were 923.0 mg/g and 728.0 mg/g, and the capacities for Cu²⁺ and Pb²⁺ were 468.5 mg/g and 1466.5 mg/g, respectively. Moreover, the UBC had a stronger affinity for Cr³⁺ and Fe³⁺ in multiple metal ions and retained at a preferable adsorption performance for dyes and heavy metals after five cycles. Precipitation, complexation, and physical adsorption were the main mechanisms of the UBC-adsorbing metal ions and dyes. Thus, lignocellulosic biochar has great potential for removing dyes and heavy metals in aqueous solutions.

Utilization of hemicelluloses from biomass energy is an important approach to explore renewable resources. A convenient, quick, and inexpensive method for the preparation of blended films from quaternized hemicelluloses (QH) and carboxymethyl cellulose (CMC) was introduced into this study. QH and CMC solution were first mixed to form homogeneous suspension, and then were dried under vacuum to fabricate the blended films. The FT-IR and XRD results indicated that the linkage between QH and CMC was due to the hydrogen bonding and electrostatic interaction. From the results of mechanical properties and water vapor permeability (WVP), the tensile strength of the blended films increased with the QH/CMC content ratio increasing in appropriate range, and the WVP of the blended films decreased. The maximum value of tensile strength of blend film achieved was 27.4 MPa. In addition, the transmittances of the blended films increased with the decreasing of QH/CMC content ratio. When the weight ratio (QH: CMC) was 1:1.5, the blend film showed the best light transmittance (45%). All the results suggested that the blended films could be used in areas of application in the coating and packaging fields from the good tensile strength, transmittance, and low WVP.