The present work was conducted to study the effects of wood species, particle size and residue particle size obtained from trimming of wood–cement composites on physical and mechanical properties of cement-bonded particleboard (CBPB). Particleboard was manufactured with a wood/cement ratio of 1:3 and specific gravity 1200 kg m⁻³. After manufacturing, the boards were tested. The second order plan was used to test the significant difference between factors and levels. It was shown that slenderness and compaction ratio increased and bulk density and specific surface decreased with the increase of particle size. With the increase in slenderness ratio and compaction ratio and decrease in bulk density and specific surface, thickness swelling and mechanical properties improved, but water absorption by the board increased. The addition of 6% of 5/3 fraction size of particle obtained from trimming of boards improved significantly the properties of the boards. The optimized panel properties, obtained using poplar particles with a fraction size of 7pass/on5, exceeded the BISON type HZ and EN Standard for Wood Particleboard. CBPB made of alder or poplar particles with 5/3 fraction size of residue exceeded the BISON type HZ. All CBPB with 5/3 fraction size of residue showed lower mean values of thickness swelling, well below the maximum requirements of both standards. In addition, wood species, fraction size of particles and residue size are believed to have been the main cause of change in the properties of the boards.

This paper presents the effects of the concentration of solid nanoparticles in the liquid feedstock injection on the high-velocity suspension flame spray (HVSFS) process. Four different concentrations of solid nanoparticles in suspension droplets with various droplet diameters are used to study gas dynamics, vaporization rate, and secondary breakup. Two types of injections, viz. surface and group, are used. The group-type injection increases the efficiency of droplet disintegration and the evaporation process and reduces the gas cooling. The initiation of the fragmentation process is difficult for small droplets carrying a high concentration of nanoparticles. Also, smaller droplets undergo rapid vaporization, leaving clogs of nanoparticles in the middle of the barrel. For larger droplets, severe fragmentation occurs inside the combustion chamber. For a higher concentration of nanoparticles, droplets exit the gun without complete evaporation. The results suggest that, in coating applications involving a higher concentration of nanoparticles, smaller droplet sizes are preferred.