It is of great significance to study the effect of solid contents (SC), binder-to-tailings (b/t) ratio, types and dosage of fly ash (FA) on the viscosity (V) and uniaxial compressive strength (UCS) of backfill. It can improve filling efficiency and reduce filling costs to understand the relationship between SC, b/t ratio, FA dosage and viscosity, and UCS of backfill. Consequently, this paper carried out uniaxial compression tests and rheological tests on five different types of backfill specimens. Experimental results indicate that, with the increase of SC, the viscosity and UCS of all backfill samples increases as a power function. With the decrease of b/t ratio, the viscosity and UCS of all backfill samples decreases as an exponential function. The coupling effect of SC and b/t ratio has a great influence on the viscosity and UCS of backfill samples. The relationship between SC, b/t ratio and viscosity, and UCS is a quadratic polynomial function. The order of the viscosity of the backfill slurry is: pure tailings < backfill slurry mixed with Ordinary Portland Cement (OPC) < backfill slurry mixed with FA1 < backfill slurry mixed with FA2. The higher the FA dosage, the greater the viscosity. The order of the UCS of backfill is: backfill with OPC > backfill with FA1 > backfill with FA2. The higher the FA dosage, the smaller the UCS. The UCS of all backfill samples increased with the increase of curing time (CT). The relations between the viscosity and UCS of backfill present the positively linear functions. It is feasible to use viscosity to predict the UCS of backfill, and the error between the UCS predicted value and the test value is mostly controlled within 10%. Ultimately, the findings of the experimental work will provide a scientific reference for the mine to design the strength of the backfill.

The flowability and mechanical properties are increasingly crucial in the filling process of deep metal mines with mining depths exceeding 1000 m. The rheological properties of filling slurry in the pipeline were analyzed through rheological tests, L-tube self-flow tests, and semi-industrial loop tests. The results revealed that with an increase in the cement-to-tailings mass ratio (c/t ratio) and mass concentration, the slurry exhibited a higher flow resistance and decreased stowing gradient. During slurry transportation, the pressure loss in the straight pipe was positively correlated with the slurry flow rate, c/t ratio, and mass concentration. A uniaxial compressive strength (UCS) test was conducted to analyze the mechanical properties of the cemented paste backfill containing BMC (CCPB) in both standard and deep-underground curing environments. The UCS of the CCPB showed an increasing trend with the rise in curing age, mass concentration, and the c/t ratio. The comprehensive analysis concluded that when the c/t ratio is 1:4, and the mass concentration is approximately 74%, and parameters such as the slump, bleeding rate, and flowability of the filling slurry meet the criteria for conveying and goaf filling, resulting in a high-strength filling body.

The stability of composite material that is composed of roof rock, cemented paste backfill (CPB), and floor rock has an important impact on safe mining within metal mines. In order to explore the mechanical properties, acoustic emission (AE), energy dissipation, and damage evolution of roof–CPB–floor (RCF) layered composite materials, uniaxial compression (loading rate 0.02 mm/min) AE tests on RCF materials with different CPB height ratios were performed. The test results show that: (1) the uniaxial compressive strength (UCS) and elastic modulus (E_R) of the RCF material were lower than those of the roof or floor rock and higher than that of the CPB. With the increase in the CPB’s height ratio from 0.2 to 0.7, the UCS and the E_R decreased from 18.42 MPa to 10.08 MPa and 3.15 GPa to 1.79 GPa, respectively, and the peak strain first decreased from 0.695 to 0.510 and then increased from 0.510 to 0.595. The UCS increased as a polynomial function with the increase in the E_R. (2) The AE ring count first increased slowly, then increased rapidly, and finally maintained a high-speed increase. The AE cumulative ring count at the peak point decreased with the increase in the CPB height ratio. The energy dissipation showed that the elastic energy U_E accumulated slowly at first, then the dissipated energy U_D increased, and finally the U_E decreased and the U_D increased almost linearly. The U_T, U_E, U_D, U_E–U_T ratio and U_D–U_T ratio showed a decreasing trend, and the U_E–U_D ratio showed an increasing trend at the peak point with the increase in the CPB height ratio. (3) Two damage constitutive models were established based on the AE ring count and energy principle. The damage evolution process of RCF materials can be divided into three stages: the slow damage accumulation stage, stable damage growth stage, and rapid damage accumulation stage.