The paper investigates the synthesis of eco-friendly composites and their properties before and after immersion in solvents of different chemical natures. For their preparation, unsaturated polyester resin (UPR) based on recycled poly (ethylene terephthalate) (PET) and peanut shell powder (PSP) were used. Polymerization was carried out in the presence of environmentally friendly polymeric cobalt. Distilled water, acetone, 10% hydrochloric acid, 40% sodium hydroxide, toluene, and 2% sodium carbonate were used as solvents in the chemical resistance test. Changes in the structure, properties, and appearance (morphology) of composites after 140 days of immersion in solvents were investigated. The results show that both the resin and its composites show resistance towards 10% HCl and toluene. The immersion in water has no significant effect on the resin, but for PSP composites, the plasticizing effect of water was observed. In acetone, after only one day, the resin and its composite with 10% PSP shrink and fall into pieces. However, the most destructive is an alkaline environment. After the immersion test, a huge increase in mass and a deterioration of gloss and thermomechanical properties were observed. The destructive influence of the 40% NaOH environment mainly concerned the resin.

This study compares the degradation process of unsaturated polyester resin (UPR) and vinyl ester resin (VER) and their biocomposites with kraft lignin. In order to study their degradation, accelerated aging, immersion in different solvents, microwave radiation and high temperature were applied. The results show that, depending on the conditions, the degradation assumes a different course. The VER resin is more chemically resistant than the UPR resin. In the case of the composites immersed in an aggressive solvent (acetone), it can be observed that the polymer matrix is degraded, whereas in water only a small increase of weight takes place. Immersion in NaOH initiates the degradation process consisting in the hydrolysis of ester bonds, which are especially observed for pure resins. Under the influence of UV radiation and microwaves, the resins are additionally cross-linked. Thermogravimetric analysis shows that in the case of composites heated to 1000 °C, a residual mass remains, which is carbonized with lignin. In turn, composites treated with microwaves lost weight.

The paper investigates the synthesis of green composites and their properties before and after the laboratory accelerated aging tests. Materials were made of unsaturated polyester resins (UPRs) based on recycled poly(ethylene terephthalate) (PET) and wood flour (WF). The effect of dibenzylideneacetone (dba) addition on mechanical and thermomechanical properties was also determined. Green composites were obtained using environment friendly polymeric cobalt as an accelerator. Before and after exposition to the xenon lamp radiation, the UPRs physically modified by WF were characterized only by a greater flexural modulus compared with the analogous composites based on the pure resin. Addition of dba caused the increase of flexural modulus, flexural strength, strain at break and mechanical loss factor compared to the non-modified material. After aging only the last mentioned parameter took on lower values compared to the pure resin analogues.

The paper investigates the properties of unsaturated polyester resins and microcrystalline cellulose (MCC) composites. The influence of MCC modification on mechanical, thermomechanical, and thermal properties of obtained materials was discussed. In order to reduce the hydrophilic character of the MCC surface, it was subjected to esterification with the methacrylic anhydride. This resulted in hydroxyl groups blocking and, additionally, the introduction of unsaturated bonds into its structure, which could participate in copolymerization with the curing resin. Composites of varying amounts of cellulose as a filler were obtained from modified MCC and unmodified (comparative) MCC. The modification of MCC resulted in obtaining composites characterized by greater flexural strength and strain at break compared with the analogous composites based on the unmodified MCC.

The study describes the thermal properties of functional microspheres composed of glycidyl methacrylate (GMA) and crosslinking agent ethylene glycol dimethacrylate (EGDMA). Copolymeric poly(GMA-co-EGDMA) microspheres were prepared via suspension–emulsion polymerization in the presence of toluene and decan-1-ol as porogens. In order to introduce functional groups, the porous methacrylate network was modified by epoxy ring opening with the use of sodium cyclopentadienide and then the Diels–Alder addition with maleic anhydride. The thermal properties of poly(GMA-co-EGDMA) materials were evaluated by thermogravimetry and differential scanning calorimetry. By TG/FTIR, it was observed that new functional materials exhibited multi-staged decomposition patterns, different from parent poly(GMA-co-EGDMA) microspheres. The synthesized poly(GMA-co-EGDMA) microspheres exhibited rather high thermal stability in inert atmosphere. Their initial decomposition temperature determined at the temperature of 2% of mass loss was about 210 °C; however, after the chemical modification it was slightly lower. The thermal degradation of parent poly(GMA-co-EGDMA) copolymer runs mainly according to the depolymerization mechanism, while functionalized by cyclopentadienyl group and maleic anhydride microspheres decompose through the chain scission mechanism.