Coal gangue is a kind of industrial solid waste with serious ecological and environmental implications. Producing concrete with coal gangue aggregate is one of the green sustainable development requirements. This paper reviews the properties and preparation methods of Chinese gangue aggregate, studies the influence of gangue aggregate on concrete properties and the prediction model of gangue concrete, and summarizes the influence of modified materials on gangue concrete. The studies analyzed in this review show that different treatments influence the performance of coal gangue aggregate concrete. With the increase in the replacement ratio of coal gangue aggregate in concrete, the concrete workability and mechanical performance are reduced. Furthermore, the pore structure changes lead to decreased porosity, greatly affecting the durability. Coal gangue is not recommended for producing high-grade concretes. Nevertheless, pore structure can be improved by adding mineral admixtures, fibers, and admixtures to the coal gangue concrete. Hence, the working properties, mechanical properties, and durability of the concrete can be improved effectively, ensuring that coal gangue concrete meets engineering design requirements. Adding modified materials to coal gangue concrete is a viable future development direction.

The Grey Relation Entropy (GRE) theory is used to analyze the sensitive pore size that affects the compressive strength of concrete. The relationship between the strength and pore structure is revised based on the sensitivity coefficient. The revised model is used to calculate the compressive strength of concrete. In order to verify the validity of the proposed model, the calculated results are compared with experimental ones, showing satisfactory agreement with a larger correlation than existing methods.

In this study, the high-temperature test (i.e., temperature to 1000 °C) is conducted on 600 MPa seismic steel bars, and its residual mechanical properties and constitutive relations are investigated though three cooling rates, i.e., under air, furnace, and water-cooling conditions. Results show that three cooling methods have significant effects on the apparent characteristics of 600 MPa steel bars, when the heating temperature is greater than 600 °C. In addition, the ultimate and yield strength of steel bars have been significantly affected by different cooling methods, with increasing heating temperature. However, the elastic modulus is significantly not affected by temperature. Furthermore, the elongation rate after fracture and the total elongation rate at the maximum force do not change significantly, when the heating temperature is less than 650 °C. The elongation rate, after fracture, and the total elongation rate, at the maximum force, have different changes for three cooling methods. The degeneration of the stress–strain curves occurs when the heating temperature is high. The two-fold line, three-fold line, and Ramberg–Osgood models are developed based on the stress–strain curve characteristics of steel bars after cooling. The fire resistance of 600 MPa steel bars of reinforced concrete structure is analyzed, which provides a basis for post-disaster damage assessment, repair, and reinforcement of the building structure.

Due to the high water absorption of coal gangue aggregate, concrete prepared with a high content of this material exhibits a significantly reduced service life under freeze–thaw conditions. This study evaluates the frost resistance of gel-enhanced coal gangue aggregate concrete modified by incorporating nano-SiO₂ and polypropylene fibre (PPF) to generate more C-S-H gel and form a dense structure with different dosages of air-entraining agent (0, 0.004%, 0.008%, 0.012%, and 0.016%). The research results show that when the admixture content is 0.012%, the concrete still exhibits excellent frost resistance after 100 freeze–thaw cycles. The mass loss is only 4.7%, compressive strength loss is 37%, and dynamic elastic modulus loss is 39%, while the specimen maintains the best apparent integrity. In addition, the capillary water absorption rate, initial capillary water absorption rate, and cumulative water absorption all reach their lowest values under this condition, indicating optimal frost resistance performance. Finally, through regression analysis, a highly accurate predictive model for capillary water absorption was established, providing a theoretical basis for further research on the durability and frost resistance of coal gangue aggregate concrete.

The layer-by-layer construction process of roller-compacted concrete (RCC) leads to the formation of layer zones, resulting in the transversely isotropic constitutive behavior of the RCC dam. Crucially, the thickness of the layer zone exerts a non-negligible influence on the overall deformation behavior of the RCC dam structure. An analytical expression for the thickness of the layer zone is derived based on the equivalent elastic modulus theory, and the influence of concrete with the same and different properties on the thickness of the layer zone is investigated. Numerical analysis is employed in conjunction with the RCC dam project to quantitatively assess the influence of layer thickness on the displacement of the dam structure. The numerical results demonstrate that considering the thickness of the layer zone leads to a substantial increase in both horizontal and vertical displacements of the dam. Furthermore, the range of extreme values of layer thickness is established using the variational principle of elasticity mechanics. When the elastic modulus ratio of RCC with layer zones to bulk concrete β is 0.85–0.99, a reasonable thickness of the layer can be obtained. When the weakening coefficient k and β are close to 1, the thickness of the layer is close to 10 cm, which is close in nature to the RCC dam.