A novel membrane based on silicon dioxide (SiO₂) and hydroxypropyl guar gum (HPG) as binder is presented and tested as a separator for lithium-ion batteries. The separator is made with renewable and low cost materials and an environmentally friendly manufacturing processing using only water as solvent. The separator offers superior wettability and high electrolyte uptake due to the optimized porosity and the good affinity of SiO₂ and guar gum microstructure towards organic liquid electrolytes. Additionally, the separator shows high thermal stability and no dimensional-shrinkage at high temperatures due to the use of the ceramic filler and the thermally stable natural polymer. The electrochemical tests show the good electrochemical stability of the separator in a wide range of potential, as well as its outstanding cycle performance.

This work elucidates the manufacturing of lithium titanate (Li₄Ti₅O₁₂, LTO) electrodes via the aqueous process using sodium carboxymethylcellulose (CMC), guar gum (GG) or pectin as binders. To avoid aluminum current collector dissolution due to the rising slurries’ pH, phosphoric acid (PA) is used as a pH-modifier. The electrodes are characterized in terms of morphology, adhesion strength and electrochemical performance. In the absence of phosphoric acid, hydrogen evolution occurs upon coating the slurry onto the aluminum substrate, resulting in the formation of cavities in the coated electrode, as well as poor cohesion on the current collector itself. Consequently, the electrochemical performance of the coated electrodes is also improved by the addition of PA in the slurries. At a 5C rate, CMC/PA-based electrodes delivered 144 mAh·g⁻¹, while PA-free electrodes reached only 124 mAh·g⁻¹. When GG and pectin are used as binders, the adhesion of the coated layers to the current collector is reduced; however, the electrodes show comparable, if not slightly better, electrochemical performance than those based on CMC. Full lithium-ion cells, utilizing CMC/PA-made Li[Ni_0.33Mn_0.33Co_0.33]O₂ (NMC) cathodes and LTO anodes offer a stable discharge capacity of ~120 mAh·g⁻¹_(NMC) with high coulombic efficiencies.

Low-cost and environmentally-friendly materials are investigated as carbon-coating precursors to modify the surface of commercial graphite for Li-ion battery anodes. The coating procedure and final carbon content are tuned to study the influence of the precursors on the electrochemical performance of graphite. Thermogravimetric analysis (TGA) and Brunauer–Emmett–Teller (BET) surface area analysis are used to characterize the carbon coating content and the surface area, respectively, whereas X-ray diffraction (XRD) and Raman spectroscopy allow tracking of the graphite’s structural changes and surface amorphization. In general, the coating reduces the first cycle coulombic efficiency by 3%–10% compared to pristine graphite due to the increase of the surface area available for the continuous electrolyte decomposition. However, the use of citric acid as a carbon source (5 wt %) improves the rate capability of graphite, resulting in the specific delithiation capacity at 3C of 228 mAh g⁻¹ vs. 211 mAh g⁻¹ for the uncoated graphite. The attempt to reduce the coating amount from 5 wt % to 2 wt % results in a lower rate capability, but the first cycle coulombic efficiency is similar to that of pristine graphite.