A novel polymer host from carboxymethyl cellulose (CMC)/poly(N-isopropylacrylamide) (PNiPAM) was developed for a high safety solid polymer electrolyte (SPE) in a zinc ion battery. Effects of the PNiPAM loading level in the range of 0–40% by weight ( wt%) on the chemical, mechanical, thermal, and morphological properties of the CMC/PNiPAMx films (where x is the wt% of PNiPAM) were symmetrically investigated. The obtained CMC/PNiPAMx films showed a high compatibility between the polymers. The CMC/PNiPAM20 blend showed the greatest tensile strength and modulus at 37.9 MPa and 2.1 GPa, respectively. Moreover, the thermal degradation of CMC was retarded by the addition of PNiPAM. Scanning electron microscopy images of CMC/PNiPAM20 revealed a porous structure that likely supported Zn²⁺ movement in the SPEs containing zinc triflate, resulting in the high Zn²⁺ ion transference number (0.56) and ionic conductivity (1.68 × 10^–4 S cm⁻¹). Interestingly, the presence of PNiPAM in the CMC/PNiPAMx blends showed a greater stability during charge–discharge cyclic tests, indicating the ability of PNiPAM to suppress dendrite formation from causing a short circuit. The developed CMC/PNiPAM20 based SPE is a promising material for high ionic conductivity and stability in a Zn ion battery.

Zinc ionic conducting-based gel polymer electrolytes (GPEs) were fabricated from carboxymethyl cellulose (CMC) and three different zinc salts in a mass ratio ranging within 0–30 wt%. The effects of zinc salt and loading level on the structure, thermal, mechanical, mechanical stability, and morphological properties, as well as electrochemical properties of the GPEs films, were symmetrically investigated. The mechanical properties and mechanical stability of CMC were improved with the addition of zinc acetate, zinc sulphate, and zinc triflate, approaching the minimum requirement of a solid state membrane for battery. The maximum ionic conductivity of 2.10 mS cm⁻¹ was achieved with the addition of 15 wt% zinc acetate (ZnA), GPE_A15. The supported parameters, indicating the presence of the amorphous region that likely supported Zn²⁺ movement in the CMC chains, were clearly revealed with the increase in the number of mobile Zn²⁺ carriers in FT-IR spectra and the magnitude of ionic transference number, the decrease of the enthalpy of fusion in DSC thermogram, and the shifting to lower intensity of 2θ in XRD pattern. The developed CMC/ZnA complex-based GPEs are very promising for their high ionic conductivity as well as good mechanical properties and the ability for long-term utilization in a zinc ion battery.

The recent development of separators with high flexibility, high electrolyte uptake, and ionic conductivity for batteries have gained considerable attention. However, studies on composite separators with the aforementioned properties for aqueous electrolytes in Zn-ion batteries are limited. In this research, a polyacrylonitrile (PAN)/bio-based polyurethane (PU)/Ti₃C₂T_x MXene composite membrane was fabricated using an electrospinning technique. Ti₃C₂ MXene was embedded in fibers and formed a spindle-like structure. With Ti₃C₂T_x MXene, the electrolyte uptake and ionic conductivity reached the superior values of 2214% and 3.35 × 10⁻³ S cm⁻¹, respectively. The composite membrane presented an excellent charge–discharge stability when assembled in a Zn//Zn symmetrical battery. Moreover, the developed separator exhibited a high flexibility and no dimensional and structural changes after heat treatment, which resulted in the high-performance separator for the Zn-ion battery. Overall, the PAN/bio-based PU/Ti₃C₂T_x MXene composite membrane can be potentially used as a high-performance separator for Zn-ion batteries.