The direct printing of microscale quantum dot light‐emitting diodes (QLEDs) is a cost‐effective alternative to the placement of pre‐formed LEDs. The quality of printed QLEDs currently is limited by nonuniformities in droplet formation, wetting, and drying during inkjet printing. Here, optimal ink formulation which can suppress nonuniformities at the pixel and array levels is demonstrated. A solvent mixture is used to tune the ejected droplet size, ensure wetting, and provoke Marangoni flows that prevent coffee stain rings. Arrays of green QLED devices are printed at a resolution of 500 pixels in.⁻¹ with a maximum luminance of ≈3000 cd m⁻² and a peak current efficiency of 2.8 cd A⁻¹. The resulting array quality is sufficient to print displays at state‐of‐the‐art resolutions.

We fabricated flexible, transparent, and conductive metal grids as Transparent Conductive Materials (TCM) with adjustable properties by direct nanoimprinting of self-assembling colloidal metal nanowires. Ultrathin gold nanowires (diameter below 2 nm) with high mechanical flexibility were confined in a stamp and readily adapted to its features. During drying, the wires self-assembled into dense bundles that percolated throughout the stamp. The high aspect ratio and the bundling yielded continuous, hierarchical superstructures that connected the entire mesh even at low gold contents. A soft sintering step removed the ligand barriers but retained the imprinted structure. The material exhibited high conductivities (sheet resistances down to 29 Ω/sq) and transparencies that could be tuned by changing wire concentration and stamp geometry. We obtained TCMs that are suitable for applications such as touch screens. Mechanical bending tests showed a much higher bending resistance than commercial ITO: conductivity dropped by only 5.6 % after 450 bending cycles at a bending radius of 5 mm.