Metal–organic frameworks (MOFs) with the Zr₆O₄(OH)₄ secondary building unit (SBU) have been of particular interest for potential commercial and industrial uses because they can be easily tailored and are reported to be chemically and thermally stable. However, we show that there are significant changes in chemical and thermal stability of Zr₆O₄(OH)₄ MOFs with the incorporation of different organic linkers. As the number of aromatic rings is increased from one to two in 1,4-benzene dicarboxylate (UiO-66, ZrMOF–BDC) and 4,4′-biphenyl dicarboxylate (UiO-67, ZrMOF–BPDC), the Zr₆O₄(OH)₄ SBU becomes more susceptible to chemical degradation by water and hydrochloric acid. Furthermore, as the linker is replaced with 2,2′-bipyridine-5,5′-dicarboxylate (ZrMOF–BIPY) the chemical stability decreases further as the MOF is susceptible to chemical breakdown by protic chemicals such as methanol and isopropanol. The results reported here bring into question the superior structural stability of the UiO-67 analogs as reported by others. Furthermore, the degradation mechanisms proposed here may be applied to other classes of MOFs containing aromatic dicarboxylate organic linkers, in order to predict their structural stability upon exposure to solvents.

Metal–organic frameworks (MOFs) with metal–carboxylate bonds, including Cu-BTC (HKUST-1), Mg-MOF-74 (Mg/DOBDC), and UiO-66, have been shown to have varying degrees of water stability. The three MOFs in this study are three of the most highly studied MOFs in the literature. We investigate here how each MOF degrades at several temperature and humidity conditions over the course of 28 days. At conditions of 90% relative humidity (RH) and 25 °C, water uptake for Cu-BTC is shown to be higher than at 90% RH and 40 °C, causing the degradation of the inner structure of Cu-BTC to occur more readily at the lower temperature. However the external surfaces of Cu-BTC degrade more readily, as shown through SEM images, at conditions of 90% RH and 40 °C. Mg-MOF-74 has a nearly complete loss of surface area after just one day of exposure to each of the conditions studied, however the PXRD patterns show only a change in the [100] peak. We offer here a novel mechanism for the degradation of Mg-MOF-74, involving a 6-coordinate Mg intermediate, which leaves the 1-dimensional channels of Mg-MOF-74 intact. Furthermore, we conclude that UiO-66 is stable to each of the aging conditions for the full 28 days of this study.