To expand the applications of graphene-based materials to biogas purification, a series of reduced graphene oxide aerogels (rGOAs) were prepared from industrial grade graphene oxide using a simple hydrothermal method. The influences of the hydrothermal preparation temperature on the textural properties, hydrophobicity and physisorption behavior of the rGOAs were investigated using a range of physical and spectroscopic techniques. The results showed that the rGOAs had a macro-porous three-dimensional network structure. Raising the hydrothermal treatment temperature reduced the number of oxygen-containing groups, whereas the specific surface area (S_BET), micropore volume (V_micro) and water contact angle values of the rGOAs all increased. The dynamic adsorption properties of the rGOAs towards hexamethyldisiloxane (L2) increased with increasing hydrothermal treatment temperature and the breakthrough adsorption capacity showed a significant linear association with S_BET, V_micro and contact angle. There was a significant negative association between the breakthrough time and inlet concentration of L2, and the relationship could be reliably predicted with a simple empirical formula. L2 adsorption also increased with decreasing bed temperature. Saturated rGOAs were readily regenerated by a brief heat-treatment at 100 °C. This study has demonstrated the potential of novel rGOA for applications using adsorbents to remove siloxanes from biogas.

Volatile methyl siloxanes (VMSs) as a trace impurity in biogas decreases its energy utilization, and thus need to be removed. In this paper, a one-step hydrothermal reduction was performed to produce three-dimensional reduced graphene oxide aerogels (rGOAs) using industrial-grade graphene oxide (IGGO) as raw material and vitamin C (VC) as a reductant to facilitate the fabrication of rGOAs. The synthesis of rGOAs was a simple, green, and energy-efficient process. The developed rGOAs were characterized using the Brunauer–Emmett–Teller method, Raman spectrometry, scanning electron microscopy, Fourier-transform infrared spectroscopy, X-ray diffraction measurements and contact angle. The results obtained showed that rGOA-1 with a VC/IGGO ratio of 1/1 (m/m) exhibited a hierarchical porous structure and super-hydrophobicity, yielding a high specific surface area (137.9 m² g⁻¹) and superior water contact angle (143.8°). The breakthrough adsorption capacity of rGOA-1 for hexamethyldisiloxane (L2, a VMS model) was 11 times higher than that of IGGO. Low inlet concentration and bed temperature were considered beneficial for the L2 adsorption. Interestingly, rGOA-1 was less sensitive to water, and it was readily regenerated for reuse by annealing at 80 °C. The rGOAs have been demonstrated to have great potential for the removal of siloxanes from biogas.

In this study, β-cyclodextrin-modified reduced graphene oxide aerogels (β-CD-rGOAs) were synthesized via a one-step hydrothermal method and were used to remove hexamethyldisiloxane (L2) from biogas. The β-CD-rGOAs were characterized by the Brunner–Emmet–Teller technique, using Fourier-transform infrared spectroscopy, Raman spectrometry, scanning electron microscopy (SEM), contact angle measurements, and X-ray diffraction. The results of the characterizations indicate that β-CD was grafted onto the surface of rGOAs as a cross-linking modifier. The β-CD-rGOA had a three-dimensional, cross-linked porous structure. The maximum breakthrough adsorption capacity of L2 on β-CD-rGOA at 273 K was 111.8 mg g⁻¹. A low inlet concentration and bed temperature facilitated the adsorption of L2. Moreover, the β-CD-rGOA was regenerated by annealing at 80 °C, which renders this a promising material for removing L2 from biogas.