» Articles | Agricultural Journals

This paper presents the results of the analysis of the chemical composition and content of heavy metal contamination in forest logging residues, in order to assess the possibility for their further utilisation. The samples were divided into 9 groups, which included coniferous tree cones, wood, and other multi-species logging residues. The elementary composition, ash content, and calorific value were determined as energy use indicators for the samples. Additionally, the content of heavy and alkali metals, which may affect combustion processes and pollutant emissions, was tested. The high content of heavy metals may also disqualify these residues for other uses. The research shows that the test residues are suitable for energy use due to their high calorific value and low content of heavy metals. However, an increased ash content in some samples and the presence of alkali metals, causing high-temperature corrosion of boilers, may disqualify them as a potential fuel in the combustion process. The forest residues may be used in other thermal processes such as pyrolysis or gasification. A low content of heavy metals and a high content of organic matter permit the use of these residues for the production of adsorbents or composite materials.

Spent coffee ground is a massively produced coffee industry waste product whose reusage is beneficial. Proximate and ultimate and stochiometric analysis of torrefied spent coffee ground were performed and results were analyzed and compared with other research and materials. Spent coffee ground is a material with high content of carbon (above 50%) and therefore high calorific value (above 20 MJ·kg⁻¹). Torrefaction improves the properties of the material, raising its calorific value up to 32 MJ·kg⁻¹. Next, the phytotoxicity of the aqueous extract was tested using the cress test. The non-torrefied sample and the sample treated at 250 °C were the most toxic. The sample treated at 250 °C adversely affected the germination of the cress seeds due to residual caffeine, tannins and sulfur release. The sample treated at 350 °C performed best of all the tested samples. The sample treated at 350 °C can be applied to the soil as the germination index was higher than 50% and can be used as an alternative fuel with net calorific value comparable to fossil fuels.

» Articles | Agricultural Journals

Tea waste as a potential biofuel and bio fertilizer was analyzed. Samples were collected from various tea species and torrefied to five different temperatures. All samples were analyzed for their proximal composition and calorific value. From the results, stoichiometric properties were calculated. A phytotoxicity test was performed, and the germination index was measured. Tea waste torrefied at 350 °C may be suitable biofuel reaching the calorific value of 25–27 MJ kg⁻¹, but with quite a high share of ash, up to 10%, which makes its use technically challenging and may lead to operating issues in a combustion chamber. The same biochar may be a suitable fertilizer for increasing the germination index, therefore, applicable to the soil. The non-torrefied sample and the sample treated at 250 °C are not suitable as fertilizers for being toxic. The total phenolic content in waste black tea was reduced from 41.26 to 0.21 mg g⁻¹, depending on the torrefaction temperature. The total flavonoid content was also reduced from 60.49 to 0.5 mg g⁻¹. The total antioxidant activity in the non-torrefied sample was 144 mg g⁻¹, and after torrefaction at 550 °C, it was 0.82 mg g⁻¹. The results showed that black tea waste residues have the potential for further use, for example, in agriculture as a soil amendment or as a potential biofuel.