Teeth clenching during exercise is important for sports performance and health. Recently, several mouth guard (MG)-type wearable devices for exercise were studied because they do not disrupt the exercise. In this study, we developed a wearable MG device with force sensors on both sides of the maxillary first molars to monitor teeth clenching. The force sensor output increased linearly up to 70 N. In four simple occlusion tests, the trends exhibited by the outputs of the MG sensor were consistent with those of an electromyogram (EMG), and the MG device featured sufficient temporal resolution to measure the timing of teeth clenching. When the jaw moved, the MG sensor outputs depended on the sensor position. The MG sensor output from the teeth-grinding test agreed with the video-motion analysis results. It was comparatively difficult to use the EMG because it contained a significant noise level. Finally, the usefulness of the MG sensor was confirmed through an exercise tolerance test. This study indicated that the developed wearable MG device is useful for monitoring clenching timing and duration, and the degree of clenching during exercise, which can contribute to explaining the relationship between teeth clenching and sports performance.

The purpose of the present study was to develop an antibacterial mouthguard (MG) material using a masterbatch of silvernanoparticle–embedded ethylene-vinyl acetate (EVA) copolymers. In order to verify that the testing material was clinically applicable as an antibacterial MG material, we conducted an antibacterial test, a shock absorption test, and analysis of in vitro silver release. The colony-forming activity of Streptococcus sobrinus, Porphyromonas gingivalis, and Escherichia coli were significantly inhibited on the testing materials compared with the commercial EVA sheet (p<0.05). The shock absorption capability of the testing material was not significantly different from that of the commercial EVA sheet. Cumulative silver release (in pure water) from the testing materials were infinitesimal after soaking for 20 days, which implied that there could be no harm in wearing the MG during exercise. These results showed that this testing material could be clinically applicable as an antibacterial MG material.

Laminated custom-made mouthguards tend to delaminate with use; this is a problem in clinical use. Insufficient bonding strength causes delamination, and bonding strength is strongly affected by heating temperature during lamination. The present study aimed to evaluate the influence of heating temperature on the sheet lamination process. Seven mouthguard sheet products were laminated together at different heating temperatures. To evaluate the bonding strength, a delamination test (n = 6) was performed, and the fracture patterns were inspected visually. To evaluate the shock absorption capability, a falling impact test (n = 5) was performed, and the specimen thicknesses were measured. All recorded values were analyzed using two-way analysis of variance and Tukey’s Honest Significant Difference Test (P < 0.05). The present study confirmed that bonding strength was dependent on heating temperature: In ethylene-vinyl acetate copolymer products, the bonding strength was almost constant at 130°C and above, and it was constant at 110°C and above in polyolefin products. The thickness of every specimen decreased and, in some specimens, the shock absorption capability decreased with increasing heating temperature. The present study concludes that the heating temperature during the sheet lamination process when laminated custom-made mouthguards are fabricated may not be less than 120°C in ethylene-vinyl acetate copolymer products and 110°C in polyolefin products.

Japan's largest platform for academic e-journals: J-STAGE is a full text database for reviewed academic papers published by Japanese societies