Components of civil buildings are frequently made of low-alloyed steel, which can suffer from corrosion damage. This damage reduces their bearing capacity and/or redistributes the load to neighboring regions with the potential risk of their collapse. For this reason, this study deals with the non-destructive monitoring of bodies made of these steels based on Barkhausen noise emission. The superimposing contribution of corrosion extent and exerted tensile load is investigated on samples of variable yield strength in the range from 235 to 1100 MPa. It is found that the presence of a corroded layer attenuates Barkhausen noise and makes the body harder from a magnetic point of view. The reduced effective thickness of the samples as a result of corrosion damage increases the true stress. Barkhausen noise grows along with the tensile stress in the direction of exerted stress at the expense of decreasing Barkhausen noise in the perpendicular direction. The evolution of Barkhausen noise versus tensile stress is mostly shifted to the lower values of Barkhausen noise, along with the increasing degree of corrosion damage. The evolution of Barkhausen noise versus tensile stress is also affected by the initial microstructure and the corresponding yield strength of the low-alloyed steel. Corrosion attack results in the growth of FWHM, which is compensated by the decreasing evolution along with the tensile stresses. The effective values drop down with the higher extent of corrosion damage. However, the response with respect to the tensile stress is asymmetric in RD and TD due to the realignment of DWs into RD. Finally, PP tends to increase with the corrosion attack as well as the tensile stress and this parameter only exhibits the systematic behavior in RD as well as TD. On the other hand, MBN-extracted parameters as well as their combination provide no exclusive values on which the pure contribution of corrosion and tensile stress can be distinguished.

The work deals with non-destructive ultrasonic testing of butt and circumferential fillet welds in the repairing of gas pipelines. The new ultrasonic technique Phased Array was used for testing. The article compared the results of Phased Array...

In this paper, the experimental investigation results of the bead sequence input on geometry, structure, and hardness of surfaced layers after multi-pass weld surfacing are analyzed. Three S355 steel plates surfaced by GMAW (Gas Metal Arc Welding) were tested with three different combinations of six beads. The geometric, structural, and hardness analysis was carried out in the cross-section of the plates in the middle of the welded layers. The dimensions of padded layers, fusion and heat-affected zone, as well as the individual padded weld were evaluated. On the basis of metallographic samples, qualitative and quantitative structure analysis was performed. Hardness measurements in surfacing welds and heat-affected zones in the tested cross-sections of the surfacing layers were carried out. A comparative analysis of structure and hardness, taking into account the thermal implications of the bead sequence, allowed for the formulation of conclusions. Comparative studies have shown differences in properties between heat-affected zones (HAZ) for individual surfacing sequences. These differences were mainly in the dimensions of the surfacing layers, the share of structural components, as well as the uniformity of hardness distributions. Finally, the most favorable sequence in terms of structure and hardness distribution, maximum hardness, and range of hardness has been indicated.

The present article is focused on the non-destructive testing (NDT) inspection of pipelines during operation namely Magnetic Flux Leakage (MFL) method and Phased Array ultrasonic (PA) method. MFL inspection technique is electromagnetic test me...

The article describes the fundamental physical principles of the ultrasonic defectoscopy TOFD (Time of Flight Diffraction) and Phased Array. There is a report from the ultrasonic testing of girth welded joint with ultrasonic flaw detector Omni...

The translation in this article analyses the technology of laser cutting, describes properties of laser cutting equipment the oxidation process of melting and sublimation laser cutting. In the article chemical composition of cutted material in...