Hydrogen gas (H₂) is being intensively proposed as a next-generation clean energy owing to the depletion of fossil fuels. Electrochemical water splitting is one of the most promising processes for hydrogen production. Furthermore, many efforts focusing on electrochemical water splitting have been made to develop low-cost, electrochemically active, and stable catalysts for efficient hydrogen production. MoS₂ has emerged as an attractive material for developing catalysts for the hydrogen evolution reaction (HER). Hence, in this study, we design hierarchically ordinated two-dimensional (2D) MoS₂ nanosheets on three-dimensional (3D) reduced graphene oxide (rGO) (H-2D/3D-MoS₂-rGO) aerogel structures as a new class of electrocatalysts for the HER. We use the one-pot hydrothermal synthesis route for developing high-performance electroactive materials for the HER. The as-prepared H-2D/3D-MoS₂-rGO contains a unique 3D hierarchical structure providing large surface areas owing to the 3D porous networks of rGO and more active sites owing to the many edge sites in the MoS₂ nanosheets. In addition, the H-2D/3D-MoS₂-rGO structure exhibits remarkable electrochemical properties during the HER. It shows a lower overpotential than pure MoS₂ and excellent electrochemical stability owing to the large number of active sites (highly exposed edge sites) and high electrical conductivity from the rGO structure.

To effectively improve the energy density and reduce the self-discharging rate of micro-supercapacitors, an advanced strategy is required. In this study, we developed a hydroquinone (HQ)-based polymer-gel electrolyte (HQ-gel) for micro-supercapacitors. The introduced HQ redox mediators (HQ-RMs) in the gel electrolyte composites underwent additional Faradaic redox reactions and synergistically increased the overall energy density of the micro-supercapacitors. Moreover, the HQ-RMs in the gel electrolyte weakened the self-discharging behavior by providing a strong binding attachment of charged ions on the porous graphitized carbon electrodes after the redox reactions. The micro-supercapacitors with HQ gel (HQ-MSCs) showed excellent energy storage performance, including a high energy volumetric capacitance of 255 mF cm⁻³ at a current of 1 µA, which is 2.7 times higher than the micro-supercapacitors based on bare-gel electrolyte composites without HQ-RMs (b-MSCs). The HQ-MSCs showed comparatively low self-discharging behavior with an open circuit potential drop of 37% compared to the b-MSCs with an open circuit potential drop of 60% after 2000 s. The assembled HQ-MSCs exhibited high mechanical flexibility over the applied external tensile and compressive strains. Additionally, the HQ-MSCs show the adequate circuit compatibility within series and parallel connections and the good cycling performance of capacitance retention of 95% after 3000 cycles.

We report a new method to produce ordered arrays of metal nanostructures on substrates. The method employs a through-hole nanoporous alumina membrane as a mask that is attached onto the substrate, silicon in this study. The material of deposition, Au in this study, was provided by pulsed laser ablation of a target gold. At an early stage of the deposition, a significant portion of Au penetrated the alumina through-holes and formed an ordered nanodot array on the silicon surface. At the later stage, the through-hole deposition was blocked by the growth of Au film on the top surface of the alumina, so that the heights of the Au nanodots were limited to about 10 nm under current experimental conditions. Subsequent attempts to clean up the top surface of the alumina with a lower power laser illumination resulted in the formation of new nanostructures around the alumina pores, nanospheres, or nanorings, depending on the fluence of the laser and the duration of the cleanup. We will discuss the underlying mechanism of the formation of these nanostructures.