In recent years, conductive hydrogels have received increasing attention as wearable electronics due to the electrochemical properties of conductive polymers combined with the softness of hydrogels. However, conventional hydrogels are complicated to prepare, require high temperature or UV radiation to trigger monomer polymerization, and are frozen at low temperatures, which seriously hinder the application of flexible wearable devices. In this paper, a conductive sensor integrating mechanical properties, adhesion, UV shielding, anti-dehydration, and anti-freeze was prepared based on Ca²⁺-initiated radical polymerization at room temperature using the synergy of sodium lignosulfonate, acrylamide (AM), and calcium chloride (CaCl₂). Metal ions can activate ammonium persulfate to generate free radicals that allow rapid gelation of AM monomers at room temperature without external stimuli. Due to ionic cross-linking and non-covalent interaction, the hydrogels have good tensile properties (1153% elongation and 168 kPa tensile strength), high toughness (758 KJ·m^-3), excellent adhesive properties (48.5 kPa), high ionic conductivity (7.2 mS·cm^-1), and UV resistance (94.4%). CaCl₂ can inhibit ice nucleation, so that the hydrogels have anti-dehydration and frost resistance properties and even at -80 °C can maintain flexibility, high conductivity, and adhesion. Assembled into a flexible sensor, it can sense various large and small movements such as compression, bending, and talking, which is a flexible sensing material with wide application prospects.

The seeds of Gleditsia sinensis and Gleditsia microphylla, widespread in China, are an important source of galactomannans. G. sinensis gum (GSG) and G. microphylla gum (GMG) were purified and precipitated using different concentrations of ethanol and isopropanol. The GSG and GMG, precipitated in different stages, presented different characteristics, including polymer recovery, mannose/galactose ratio, chemical composition, molecular weight, and morphological appearance. The galactomannan recovery of GSG and GMG in 33.3% ethanol was 81.7% and 82.5%, respectively, while that in 28.8% isopropanol was 81.3% and 82.9%, respectively. To achieve similar precipitation efficiency, the amount of isopropanol should be lower than that of ethanol because of the lower dielectric constant of isopropanol (20 vs. 25 for ethanol). The precipitation behavior of galactomannans in polar organic solvents was dependent on the molecular structures and properties of the solvent. A higher mannose/galactose ratio and a higher molecular weight was obtained in a lower concentration of alcohols.