Plastic waste reduction and recycling through circular use has been critical nowadays, since there is an increasing demand for the production of plastic components based on different polymeric matrices in various applications. The most commonly used recycling procedure, especially for thermoplastic materials, is based on thermomechanical process protocols that could significantly alter the polymers’ macromolecular structure and physicochemical properties. The study at hand focuses on recycling of polyamide 12 (PA12) filament, through extrusion melting over multiple recycling courses, giving insight for its effect on the mechanical and thermal properties of Fused Filament Fabrication (FFF) manufactured specimens throughout the recycling courses. Three-dimensional (3D) FFF printed specimens were produced from virgin as well as recycled PA12 filament, while they have been experimentally tested further for their tensile, flexural, impact and micro-hardness mechanical properties. A thorough thermal and morphological analysis was also performed on all the 3D printed samples. The results of this study demonstrate that PA12 can be successfully recycled for a certain number of courses and could be utilized in 3D printing, while exhibiting improved mechanical properties when compared to virgin material for a certain number of recycling repetitions. From this work, it can be deduced that PA12 can be a viable option for circular use and 3D printing, offering an overall positive impact on recycling, while realizing 3D printed components using recycled filaments with enhanced mechanical and thermal stability.

The continuous demand for thermoplastic polymers in a great variety of applications, combined with an urgent need to minimize the quantity of waste for a balanced energy-from-waste strategy, has led to increasing scientific interest in developing new recycling processes for plastic products. Glycol-modified polyethylene terephthalate (PETG) is known to have some enhanced properties as compared to polyethylene terephthalate (PET) homopolymer; this has recently attracted the interest from the fused filament fabrication (FFF) three-dimensional (3D) printing community. PET has shown a reduced ability for repeated recycling through traditional processes. Herein, we demonstrate the potential for using recycled PETG in consecutive 3D printing manufacturing processes. Distributed recycling additive manufacturing (DRAM)-oriented equipment was chosen in order to test the mechanical and thermal response of PETG material in continuous recycling processes. Tensile, flexure, impact strength, and Vickers micro-hardness tests were carried out for six (6) cycles of recycling. Finally, Raman spectroscopy as well as thermal and morphological analyses via scanning electron microscopy (SEM) fractography were carried out. In general, the results revealed a minor knockdown effect on the mechanical properties as well as the thermal properties of PETG following the process proposed herein, even after six rounds of recycling.

The recycling of polymeric materials has received a steadily growing scientific and industrial interest due to the increase in demand and production of durable and lightweight plastic parts. Recycling of such materials is mostly based on thermomechanical processes that significantly affect the mechanical, as well as the overall physicochemical properties of polymers. The study at hand focuses on the recyclability of Fused Filament Fabrication (FFF) 3D printed Polypropylene (PP) for a certain number of recycling courses (six in total), and its effect on the mechanical properties of 3D printed parts. Namely, 3D printed specimens were fabricated from non-recycled and recycled PP material, and further experimentally tested regarding their mechanical properties in tension, flexion, impact, and microhardness. Comprehensive dynamic scanning calorimetry (DSC), thermogravimetric analysis (TGA), Raman spectroscopy, and morphological investigations by scanning electron microscopy (SEM) were performed for the different 3D printed PP samples. The overall results showed that there is an overall slight increase in the material’s mechanical properties, both in tension and in flexion mode, while the DSC characterization indicates an increase in the polymer crystallinity over the recycling course.

In this work, strain rate sensitivity was studied for 3D-printed polycarbonate (PC) and thermoplastic polyurethane (TPU) materials. Specimens were fabricated through fused filament fabrication (FFF) additive manufacturing (AM) technology and were tested at various strain rates. The effects of two FFF process parameters, i.e., nozzle temperature and layer thickness, were also investigated. A wide analysis for the tensile strength (MPa), the tensile modulus of elasticity (MPa), the toughness (MJ/m³) and the strain rate sensitivity index ‘m’ was conducted. Additionally, a morphological analysis was conducted using scanning electron microscopy (SEM) on the side and the fracture area of the specimens. Results from the different strain rates for each material were analyzed, in conjunction with the two FFF parameters tested, to determine their effect on the mechanical response of the two materials. PC and TPU materials exhibited similarities regarding their temperature response at different strain rates, while differences in layer height emerged regarding the appropriate choice for the FFF process. Overall, strain rate had a significant effect on the mechanical response of both materials.

Polypropylene (PP) is an engineered thermoplastic polymer widely used in various applications. This work aims to enhance the properties of PP with the introduction of titanium dioxide (TiO₂) nanoparticles (NPs) as nanofillers. Novel nanocomposite filaments were produced at 0.5, 1, 2, and 4 wt.% filler concentrations, following a melt mixing extrusion process. These filaments were then fed to a commercially available fused filament fabrication (FFF) 3D printer for the preparation of specimens, to be assessed for their mechanical, viscoelastic, physicochemical, and fractographic properties, according to international standards. Tensile, flexural, impact, and microhardness tests, as well as dynamic mechanical analysis (DMA), Raman, scanning electron microscopy (SEM), melt flow volume index (MVR), and atomic force microscopy (AFM), were conducted, to fully characterize the filler concentration effect on the 3D printed nanocomposite material properties. The results revealed an improvement in the nanocomposites properties, with the increase of the filler amount, while the microstructural effect and processability of the material was not significantly affected, which is important for the possible industrialization of the reported protocol. This work showed that PP/TiO₂ can be a novel nanocomposite system in AM applications that the polymer industry can benefit from.

The scope of this work was to create, with melt mixing compounding process, novel nanocomposite filaments with enhanced properties that industry can benefit from, using commercially available materials, to enhance the performance of three-dimensional (3D) printed structures fabricated via fused filament fabrication (FFF) process. Silicon Dioxide (SiO₂) nanoparticles (NPs) were selected as fillers for a polylactic acid (PLA) thermoplastic matrix at various weight % (wt.%) concentrations, namely, 0.5, 1.0, 2.0 and 4.0 wt.%. Tensile, flexural and impact test specimens were 3D printed and tested according to international standards and their Vickers microhardness was also examined. It was proven that SiO₂ filler enhanced the overall strength at concentrations up to 1 wt.%, compared to pure PLA. Atomic force microscopy (AFM) was employed to investigate the produced nanocomposite extruded filaments roughness. Raman spectroscopy was performed for the 3D printed nanocomposites to verify the polymer nanocomposite structure, while thermogravimetric analysis (TGA) revealed the 3D printed samples’ thermal stability. Scanning electron microscopy (SEM) was carried out for the interlayer fusion and fractography morphological characterization of the specimens. Finally, the antibacterial properties of the produced nanocomposites were investigated with a screening process, to evaluate their performance against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus).