This work reports supercritical water oxidation (SCWO) of organic pollutants in industrial wastewater in the absence and presence of catalysts. To increase the efficiency of the oxidation process, the SCWO of organic compounds in industrial wastewater was performed in the presence of various iron- and manganese-containing heterogeneous catalysts (Fe-Ac, Fe-OH, and Mn-Al). The catalytic and non-catalytic SCWO of organic compounds in wastewater from PJSC “Nizhnekamskneftekhim”, generated from the epoxidation of propylene with ethylbenzene hydroperoxide in the process of producing propylene oxide and styrene (PO/SM), was performed. The effect of operational parameters (temperature, pressure, residence time, type of catalysts, oxygen excess ratio, etc.) on the efficiency of the process of oxidation of organic compounds in the wastewater was studied. SCWO was studied in a flow reactor with induction heating under different temperatures (between 673.15 and 873.15 K) and at a pressure of 22.5 MPa. The reaction time ranged from 1.8 to 4.83 min. Compressed air was used as an oxidizing agent (oxidant) with an oxidant ratio of two to four. A pseudo-first-order model expressed the kinetics of the SCWO processes, and the rate constants were evaluated. In the present work, in order to optimize the operation parameters of the SCWO process, we used the thermodynamic properties of near- and supercritical water by taking into account the asymmetric behavior of the liquid–vapor coexistence curve.

The unique properties of pillared materials determine their use in catalysis, purification and separation. The paper studies the reduction of composite catalysts, Fe-pillared materials. The authors compare their reduction in low temperature capacitively coupled RF hydrogen discharge of low pressure to their conventional direct hydrogen reduction in a tubular muffle furnace. X-ray diffraction analysis was used to characterize the iron-bearing phases. The results show that the reduction of iron hydro/oxide clusters associated with an aluminosilicate matrix to metallic iron is very challenging due to the degree of the pore space availability for hydrogen.