Bone regeneration using inorganic nanoparticles is a robust and safe approach. In this paper, copper nanoparticles (Cu NPs) loaded with calcium phosphate scaffolds were studied for their bone regeneration potential in vitro. The pneumatic extrusion method of 3D printing was employed to prepare calcium phosphate cement (CPC) and copper loaded CPC scaffolds with varying wt% of copper nanoparticles. A new aliphatic compound Kollisolv MCT 70 was used to ensure the uniform mixing of copper nanoparticles with CPC matrix. The printed scaffolds were studied for physico-chemical characterization for surface morphology, pore size, wettability, XRD, and FTIR. The copper ion release was studied in phosphate buffer saline at pH 7.4. The in vitro cell culture studies for the scaffolds were performed using human mesenchymal stem cells (hMSCs). The cell proliferation study in CPC-Cu scaffolds showed significant cell growth compared to CPC. The CPC-Cu scaffolds showed improved alkaline phosphatase activity and angiogenic potential compared to CPC. The CPC-Cu scaffolds showed significant concentration dependent antibacterial activity in Staphylococcus aureus. Overall, the CPC scaffolds loaded with 1 wt% Cu NPs showed improved activity compared to other CPC-Cu and CPC scaffolds. The results showed that copper has improved the osteogenic, angiogenic and antibacterial properties of CPC scaffolds, facilitating better bone regeneration in vitro.

Recently, various innovative technologies have been developed for the enhanced delivery of biologics as attractive formulation targets including polymeric micro and nanoparticles. Combined with personalized medicine, this area can offer a great opportunity for the improvement of therapeutics efficiency and the treatment outcome. Herein, a novel manufacturing method has been introduced to produce protein-loaded chitosan particles with controlled size. This method is based on an additive manufacturing technology that allows for the designing and production of personalized particulate based therapeutic formulations with a precise control over the shape, size, and potentially the geometry. Sprayed multi adsorbed-droplet reposing technology (SMART) consists of the high-pressure extrusion of an ink with a well determined composition using a pneumatic 3D bioprinting approach and flash freezing the extrudate at the printing bed, optionally followed by freeze drying. In the present study, we attempted to manufacture trypsin-loaded chitosan particles using SMART. The ink and products were thoroughly characterized by dynamic light scattering, rheometer, Scanning Electron Microscopy (SEM), and Fourier Transform Infra-Red (FTIR) and Circular Dichroism (CD) spectroscopy. These characterizations confirmed the shape morphology as well as the protein integrity over the process. Further, the effect of various factors on the production were investigated. Our results showed that the concentration of the carrier, chitosan, and the lyoprotectant concentration as well as the extrusion pressure have a significant effect on the particle size. According to CD spectra, SMART ensured Trypsin’s secondary structure remained intact regardless of the ink composition and pressure. However, our study revealed that the presence of 5% (w/v) lyoprotectant is essential to maintain the trypsin’s proteolytic activity. This study demonstrates, for the first time, the viability of SMART as a single-step efficient process to produce biologics-based stable formulations with a precise control over the particulate morphology which can further be expanded across numerous therapeutic modalities including vaccines and cell/gene therapies.

Polymeric nanoparticles (NPs) have a variety of biomedical, biotechnology, agricultural and environmental applications. As such, a great need has risen for the fabrication of these NPs in large scales. In this study, we used a high throughput fiber reactor for the preparation of poly(lactic-co-glycolic acid) (PLGA) NPs via nanoprecipitation. The fiber reactor provided a high surface area for the controlled interaction of an organic phase containing the PLGA solution with an aqueous phase, containing poly(vinyl alcohol) (PVA) as a stabilizer. This interaction led to the self-assembly of the polymer into the form of NPs. We studied operational parameters to identify the factors that have the greatest influence on the properties of the resulting PLGA NPs. We found that the concentration of the PLGA solution is the factor that has the greatest effect on NP size, polydispersity index (PDI), and production rate. Increasing PLGA concentration increased NP sizes significantly, while at the same time decreasing the PDI value. The second factor that was found to affect NP properties was the concentration of PVA solution, which resulted in increased NP sizes and decreased production rates. Flowrates of the feed streams also affected NP size to a lesser extent, while changing the operational temperature did not change the product’s features. In general, the results demonstrate that fiber reactors are a suitable method for the large-scale, continuous preparation of polymeric NPs suitable for biomedical applications.