Blast furnace slag, an industrial by-product, is emerging as a potential raw material to synthesize hydroxyapatite and zeolite. In this study, the effects of temperature on the hydrothermal synthesis of hydroxyapatite-zeolite from blast furnace slag were investigated. Specimens were synthesized at different temperatures (room temperature, 50, 90, 120, or 150 °C). The synthesized specimens were analyzed qualitatively and quantitatively via X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), BET/BJH, and scanning electron microscopy/energy dispersive using X-ray analysis (SEM/EDX). It was found that the hydroxyapatite phase was synthesized at all the reaction temperatures, while faujasite type zeolite appeared in the specimens synthesized at 90 and 120 °C. Moreover, faujasite was replaced by hydroxysodalite in the specimens synthesized at 150 °C. Additionally, the crystals of the hydroxyapatite tended to become larger and total crystallinity increased as the reaction temperature increased.

This study investigated the effect of NaOH concentration on the assemblage, crystallinity, and dimension of crystalline phases in hydroxyapatite–zeolite composites made with blast furnace slag. X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy measurement, scanning electron microscopy (SEM), and nitrogen adsorption–desorption tests were conducted to characterize the synthesized composites. In addition, the cesium adsorption potential of the synthesized composites was evaluated to assess the feasibility of using hydroxyapatite–zeolite composites synthesized from blast furnace slag. The composite samples using a 3 M NaOH solution showed the formations of Na-P1 and Faujasite (FAU) zeolites along with hydroxyapatite, which led to the highest adsorption capacity for cesium (44.90 mg/g).