MCM-41 based catalysts (molar ratio Si/Al = 40) were prepared by a hydrothermal route, modified by ionic exchange with different metals (Cu, Cr, Fe and Zn) and finally calcined at 550 °C. The catalysts were fully characterized by different techniques that confirmed the formation of oxides of the different metals on the surfaces of all materials. Low-angle X-ray diffraction (XRD) analyses showed that calcination resulted in the incorporation of metallic Zn, Fe and Cr in the framework of MCM-41, while in the case of Cu, thin layers of CuO were formed on the surface of MCM-41. The solids obtained were tested in the catalytic wet peroxide oxidation (CWPO) of acetaminophen at different temperatures (25–55 °C). The activity followed the order: Cr/MCM-41 ≥ Fe/MCM-41 > Cu/MCM-41 > Zn/MCM-41. The increase of the reaction temperature improved the performance and activity of Cr/MCM-41 and Fe/MCM-41 catalysts, which achieved complete conversion of acetaminophen in short reaction times (15 min in the case of Cr/MCM-41). Fe/MCM-41 and Cr/MCM-41 were submitted to long-term experiments, being the Fe/MCM-41 catalyst the most stable with a very low metal leaching. The leaching results were better than those previously reported in the literature, confirming the high stability of Fe/MCM-41 catalysts synthesized in this study.

This work focuses on the preparation of aerogel composite beads based on Zn(II)-crosslinked alginate and loaded with different percentages of AgNPs using a simple approach. The obtained samples were evaluated in two different applications: the first application consists in their use as catalysts for the reduction of MB, MO, OG and CR dyes in a simple and binary system under the presence of NaBH₄. For this, several parameters affecting the catalytic behavior of these catalysts have been investigated and discussed such as the catalyst mass, AgNPs content, dye nature, and the selectivity of the catalyst in a binary system. The second application concerns their antibacterial activities towards two Gram-negative bacteria Escherichia coli (ATCC 25922), and Pseudomonas aeruginosa (ATCC 27853), and a Gram-positive bacteria Staphylococcus aureus (ATCC 25923). The physico-chemical properties of different samples were characterized by XRD, FTIR, SEM/EDS, and TGA analysis. The obtained results confirmed the presence of AgNPs on a highly porous alginate structure. The dispersion of a high percentage of AgNPs leads to the formation of nanoparticles on the outer surface of the alginate which led to their leaching after the catalytic test, while the composite having a low percentage of AgNPs showed good results through all dyes without leaching of AgNPs. For the antibacterial application of the different samples, it was shown that a composite with a higher percentage of AgNPs was the most effective against all bacteria.