Recently, nanostructured copper oxides formed via anodizing have been intensively researched due to their potential catalytic applications in emerging issues. The anodic Cu₂O and CuO nanowires or nanoneedles are attractive photo- and electrocatalysts since they show wide array of desired electronic and morphological features, such as highly-developed surface area. In CO₂ electrochemical reduction reaction (CO₂RR) copper and copper-based nanostructures indicate unique adsorption properties to crucial reaction intermediates. Furthermore, anodized copper-based materials enable formation of C₂₊ hydrocarbons and alcohols with enhanced selectivity. Moreover, anodic copper oxides provide outstanding turnover frequencies in electrochemical methanol oxidation at lowered overpotentials. Therefore, they can be considered as precious metals electrodes substituents in direct methanol fuel cells. Additionally, due to the presence of Cu(III)/Cu(II) redox couple, these materials find application as electrodes for non-enzymatic glucose sensors. In photoelectrochemistry, Cu₂O-CuO heterostructures of anodic copper oxides with highly-developed surface area are attractive for water splitting. All the above-mentioned aspects of anodic copper oxides derived catalysts with state-of-the-art background have been reviewed within this paper.

Anodic oxidation of metals leads to the formation of ordered nanoporous or nanotubular oxide layers that contribute to numerous existing and emerging applications. However, there are still numerous fundamental aspects of anodizing that have to be well understood and require deeper understanding. Anodization of metals is accompanied by the inevitable phenomenon of anion incorporation, which is discussed in detail in this review. Additionally, the influence of anion incorporation into anodic alumina and its impact on various properties is elaborated. The literature reports on the impact of the incorporated electrolyte anions on photoluminescence, galvanoluminescence and refractive index of anodic alumina are analyzed. Additionally, the influence of the type and amount of the incorporated anions on the chemical properties of anodic alumina, based on the literature data, was also shown to be important. The role of fluoride anions in d-electronic metal anodizing is shown to be important in the formation of nanostructured morphology. Additionally, the impact of incorporated anionic species, such as ruthenites, and their influence on anodic oxides formation, such as titania, reveals how the phenomenon of anion incorporation can be beneficial.

Hybrid materials play an essential role in the development of the energy storage technologies since a multi-constituent system merges the properties of the individual components. Apart from new features and enhanced performance, such an approach quite often allows the drawbacks of single components to be diminished or reduced entirely. The goal of this paper was to prepare and characterize polymer-metal hydroxide (polypyrrole-nickel hydroxide, PPy-Ni(OH)₂) nanowire arrays demonstrating good electrochemical performance. Nanowires were fabricated by potential pulse electrodeposition of pyrrole and nickel hydroxide into nanoporous anodic alumina oxide (AAO) template. The structural features of as-obtained PPy-Ni(OH)₂ hybrid nanowires were characterized using FE-SEM and TEM analysis. Their chemical composition was confirmed by energy-dispersive x-ray spectroscopy (EDS). The presence of nickel hydroxide in the synthesized PPy-Ni(OH)₂ nanowire array was investigated by X-ray photoelectron spectroscopy (XPS). Both FE-SEM and TEM analyses confirmed that the obtained nanowires were composed of a polymer matrix with nanoparticles dispersed within. EDS and XPS techniques confirmed the presence of PPy-Ni(OH)₂ in the nanowire array obtained. Optimal working potential range (i.e., available potential window), charge propagation, and cyclic stability of the electrodes were determined with cyclic voltammetry (CV) at various scan rates. Interestingly, the electrochemical stability window for the aqueous electrolyte at PPy-Ni(OH)₂ nanowire array electrode was remarkably wider (ca. 2 times) in comparison with the non-modified PPy electrode. The capacitance values, calculated from cyclic voltammetry performed at 20 mV s⁻¹, were 25 F cm⁻² for PPy and 75 F cm⁻² for PPy-Ni(OH)₂ array electrodes. The cyclic stability of the PPy nanowire array electrode up to 100 cycles showed a capacitance fade of about 13%.