Objectives: Hydrogels produced using the freeze–thaw method have demonstrated significant potential for wound management applications. However, their production requires precise control over critical factors including freezing temperature and the choice of matrix-forming excipients, for which no consensus on the optimal conditions currently exists. This study aimed to address this gap by evaluating the effects of the above-mentioned variables on cryogel performance. Methods: Mechanical properties, absorption capacity, and microstructure were assessed alongside advanced analyses using differential scanning calorimetry (DSC) and low-field nuclear magnetic resonance relaxometry (LF TD NMR). Results: The results demonstrated that fully hydrolyzed polyvinyl alcohol (PVA) with a molecular weight above 61,000 g/mol is essential for producing high-performance cryogels. Among the tested formulations, an 8% (w/w) PVA_56–98 solution (Mw~195,000; DH = 98.0–98.8%) with 10% (w/w) propylene glycol (PG) provided the best balance of stretchability, durability, and low adhesion. Notably, while −25 °C is often used for cryogel preparation, freezing the gel precursor at −80 °C yielded superior results, producing materials with more open, interconnected structures and enhanced mechanical strength and elasticity—deviating from conventional practices. Conclusions: The designed cryogel prototypes exhibited functional properties comparable to or even surpassing commercial wound dressings, except for absorption capacity, which remained lower. Despite this, the cryogel prototypes demonstrated potential as wound dressings, particularly for use in dry or minimally exuding wounds. All in all, this study provides a comprehensive analysis of the physicochemical and functional properties of PVA cryogels, establishing a strong foundation for the development of advanced wound dressing systems.

Amorphization serves as a strategy for the improvement of poor dissolution characteristics of many drug compounds. However, in many formulations the content of polymeric stabilizer is high, which is undesirable from the perspective of future applications. Thus, studying the composition-dependent stability of amorphous solid dispersions seems to be demanded. In this paper, we describe the amorphization of ezetimibe, a lipid-lowering drug, in the spray drying process and investigate the effect of polyvinylpyrrolidone-co-poly(vinyl acetate) (PVP/VA) content on the physical stability and dissolution characteristics of the drug. Fully amorphous systems were obtained when the concentration of the polymer in solid dispersion was as low as 20%. The amorphization led to the dissolution enhancement by even 70%, with a noticeable sudden increase at around 40% of PVP/VA content and very small variations for systems having 66–90% PVP/VA. It was also correlated to wettability characteristics of solid dispersions, which may suggest that in the vicinity of 40% of the polymer content, the behavior of the system becomes independent of the PVP/VA content.

Wound dressings when applied are in contact with wound exudates in vivo or with acceptor fluid when testing drug release from wound dressing in vitro. Therefore, the assessment of bidirectional mass transport phenomena in dressing after application on the substrate is important but has never been addressed in this context. For this reason, an in vitro wound dressing stack model was developed and implemented in the 3D printed holder. The stack was imaged using magnetic resonance imaging, i.e., relaxometric imaging was performed by means of T₂ relaxation time and signal amplitude 1D profiles across the wound stack. As a substrate, fetal bovine serum or propylene glycol were used to simulate in vivo or in vitro cases. Multi-exponential analysis of the spatially resolved magnetic resonance signal enabled to distinguish components originating from water and propylene glycol in various environments. The spatiotemporal evolution of these components was assessed. The components were related to mass transport (water, propylene glycol) in the dressing/substrate system and subsequent changes of physicochemical properties of the dressing and adjacent substrate. Sharp changes in spatial profiles were detected and identified as moving fronts. It can be concluded that: (1) An attempt to assess mass transport phenomena was carried out revealing the spatial structure of the wound dressing in terms of moving fronts and corresponding layers; (2) Moving fronts, layers and their temporal evolution originated from bidirectional mass transport between wound dressing and substrate. The setup can be further applied to dressings containing drugs.