The microstructure and mechanical properties of an API 5CT L80 casing grade steel (0.24C 0,4Si 1.4Mn CrNiCu) have been studied after performing weld thermal simulations (with and without subsequent tempering) applying a thermal cycle weld simulator. Specimens were subjected to three different peak temperatures (1300 °C, 1150 °C, 950 °C) and five different cooling rates (1 °C/s, 3 °C/s, 5 °C/s, 10 °C/s, 60 °C/s) through the austenite transformation temperature range. Based on the microstructure, hardness values, and toughness properties of the simulated specimens, thermal cycles were selected and recommended for welding of L80 components by the SAG-FW (shielded active gas forge welding) method.

The Shielded Active Gas Forge Welding (SAG-FW) method is a solid-state welding technique in which the mating surfaces are heated by induction heating or direct electrical heating before being forged together to form a weld. In this article, an API 5CT L80 grade carbon steel alloy has been welded using the SAG-FW method. A small-scale forge welding machine has been used to join miniature pipes extracted from a large pipe wall. The welding was performed at three different forging temperatures, i.e., 1300 °C, 1150 °C and 950 °C, in some cases followed by one or two post weld heat treatment cycles. In order to qualify the welds, mechanical and corrosion testing was performed on miniature samples extracted from the welded pipes. In addition, the microstructure of the welds was analysed, and electron probe microanalysis was carried out to control that no oxide film had formed along the weld line. Based on the complete set of experimental results, promising parameters for SAG-FW welding of the API 5CT L80 grade steel are suggested. The most promising procedure includes forging at relative high temperature (1150 °C) followed by rapid cooling and a short temper. This procedure was found to give a weld zone microstructure dominated by tempered martensite with promising mechanical and corrosion properties. The investigation confirmed that small scale forge welding testing is a useful tool in the development of welding parameters for full size SAG-FW welding.

The authors wish to make the following corrections to this paper