Strengthening of structural members is a common practice around the world that may arise due to deterioration of concrete with age or upgradation of design code. This paper aims to elucidate a technique used for strengthening of the reinforced concrete beam for flexural capacity by using externally welded steel angles and steel bars. For this motive, three beams were strengthened with external steel angles and three with external steel bars. The external strengthening steel elements were attached at the bottom of the beam with shear reinforcement. Control samples without external steel angles and steel bars for comparison purposes were also prepared. All reinforced concrete beams were first constructed using a concrete ratio of 1:2:4, and then external steel elements were added to existing flexural reinforcement by using a fillet weld with tee joints having thickness and length of 5/16" (7.9 mm) and 6" (152.4 mm), respectively. Fourth point loading criteria were used to investigate the flexural capacity of beams in positive bending. All beams were designed strong enough in shear, to resist the ultimate loads without shear failure. Test results indicated that beams strengthened with this technique have an average increase of 238% with steel angles and 106% with steel bars, in load-carrying capacity than control samples. Strengthened beams showed a uniform crack pattern. Moreover, the concrete cover made a good bond with existing concrete and was strong enough to withstand ultimate loads. Conclusively, the steel angles and steel bars can be used as an external strengthening material, to enhance the flexural capacity of reinforced concrete beams.

In this study, Multiwalled Carbon Nanotubes (MWCNTs) and Marble Powder (MP) have been utilized in reinforced concrete columns to assess their structural behavior. The nanotubes from 0.025% to 0.20% and 5% MP by weight of cement were used. The compressive strength of reinforced concrete columns and cubes was analyzed as the main property. The incorporation of MWCNTs and marble powder was able to increase the compressive strength of columns by 72.69% and mortar by 42.45% as compared to reference concrete. The ductility was noted to be improved by 42.04%. The load-deformation and stress-strain behaviors were also analyzed. The Scanning Electron Microscopy (SEM) analysis revealed the formation of a strong compact bridge (90–100 layers), Calcium Silicate Hydrate (C-S-H) gel, evenly dispersion, and bridging effect caused by MWCNTs. The incorporation of 0.20% MWCNTs by weight of cement was recommended to be effectively used as a reinforcing agent in concrete.