Wood used in exposed exterior applications degrades and changes color due to weathering. Expanded use of mass timber is resulting in architects increasingly designing structures with wood in exterior exposure. Coatings can reduce the effects of weathering and prolong the visual characteristics of wood. However, coating performance depends on a variety of factors including the blend of resins, oils, pigments, and binders. Coating manufacturers often claim superior performance for products, but data directly comparing different coatings on different species is rarely publicly available. Premature coating failure increases long-term building maintenance expense while potentially enhancing biological degradation and reducing service life. This study compares the performance of 12 exterior wood coatings on 5 wood species. Performance was evaluated according to changes in the components in the International Commission on Illumination (CIE) L*a*b* color space of images taken at 6-month intervals over 18 months of the wood samples. The analysis was performed using Welch’s ANOVA, Games-Howell pairwise comparisons tests, and a clustering procedure using distances between each pair of groups means for the 18 months ΔL*, Δa*, Δb* values. Most of the coatings lost their protective effects within 1 year of exposure due to combinations of biological and ultraviolet radiation (UV) degradation illustrating the difficulty of protecting timber in exterior exposures. This study provides a guide for users wishing to specify coatings for exposed wood in mass timber structures.

Wood exposed in exterior applications degrades and changes color due to weathering and fungal growth. Wood coatings can reduce the effects of weathering by reducing the damaging effects of ultraviolet light, reducing water absorption, and slowing fungal growth on the surface. Coating performance depends on the blend of resins, oils, and pigments and varies considerably among different wood species and conditions. Specific information describing expected service for different wood species and exposure conditions is not commonly available; certain combinations may work well in one climate or on one timber species, but underperform elsewhere. This study compared the performance of three industrial wood coatings on two wood species for two temperate climates under natural weathering conditions. Most of the coatings/species combinations lost their protective properties within 12 to 15 months; however, fungal growth was more prevalent at the wetter site than at the drier site for several combinations. Film-forming coatings often peeled and cracked, while penetrating coatings weathered and changed color relatively uniformly during the study. While no coating was completely effective, the results illustrate the benefits of using coatings that promote the development of natural, uniform-patinaed wood surfaces. The findings also guide coating maintenance programs for mass timber structures exposed to natural weathering conditions.