In this work, advanced polymer nanocomposites comprising of polyvinyl alcohol (PVA) and nanodiamonds (NDs) were developed using a single-step solution-casting method. The properties of the prepared PVA/NDs nanocomposites were investigated using Raman spectroscopy, small- and wide-angle X-ray scattering (SAXS/WAXS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and dynamic mechanical analysis (DMA). It was revealed that the tensile strength improved dramatically with increasing ND content in the PVA matrix, suggesting a strong interaction between the NDs and the PVA. SEM, TEM, and SAXS showed that NDs were present in the form of agglomerates with an average size of ~60 nm with primary particles of diameter ~5 nm. These results showed that NDs could act as a good nanofiller for PVA in terms of improving its stability and mechanical properties.

Bulk layered transition metal dichalcogenides (TMDs) show diamagnetic properties. When exfoliated, the materials’ band gap increases and changes from an indirect band gap to a direct one. During the exfoliation, the TMDs may undergo a phase transition from 2H to 1T polymorph, which is likely electronically driven and accompanied by a metal–insulator transition. A significantly higher efficiency of the exfoliation was observed using sodium naphthalenide compared to butyllithium. Moreover we demonstrate that the exfoliation has a dramatic influence on the magnetic properties of two TMDs, MoS₂ and WS₂. These materials become partly ferromagnetic upon exfoliation, which is a highly unexpected behavior. Exotic ferromagnetism is generally observed on samples with a high degree of exfoliation, which indicates the association of this effect with defects formed on the edges of dichalcogenide sheets. Such an exotic ferromagnetic behavior, if properly understood and brought under material engineering control, shall open the door to new applications of these materials.

Solar cells based on black silicon (b‐Si) are proven to be promising in photovoltaics (PVs) by exceeding 22% efficiency. To reach high efficiencies with b‐Si surfaces, the most crucial step is the effective surface passivation. Up to now, the highest effective minority carrier lifetimes are achieved with atomic layer‐deposited Al₂O₃ or thermal SiO₂. Plasma‐enhanced chemical vapor deposition (PECVD)‐grown hydrogenated amorphous silicon (a‐Si:H) passivation of b‐Si is seldom reported due to conformality problems. In this current study, b‐Si surfaces superposed on standard pyramidal textures, also known as modulated surface textures (MSTs), are successfully passivated by PECVD‐grown conformal layers of a‐Si:H. It is shown that under proper plasma‐processing conditions, the effective minority carrier lifetimes of samples endowed with front MST and rear standard pyramidal textures can reach up to 2.3 ms. A route to the conformal growth is described and developed by transmission electron microscopic (TEM) images. Passivated MST samples exhibit less than 4% reflection in a wide spectral range from 430 to 1020 nm.