Fluorescent carbon quantum dots (CQDs) are synthesized by laser irradiation of carbon glassy particles suspended in polyethylene glycol 200 by two methods, a batch and a flow jet configuration. The flow jet configuration is carried out by the simple combination of common laboratory objects to construct a home-made passage reactor of continuous flow. Despite the simplicity of the system, the laser energy is better harvested by the carbon microparticles, improving the fabrication efficiency a 15% and enhancing the fluorescence of CQDs by an order of magnitude in comparison with the conventional batch. The flow jet-synthesized CQDs have a mean size of 3 nm and are used for fluorescent imaging of transparent healthy and cancer epithelial human cells. Complete internalization is observed with a short incubation time of 10 min without using any extra additive or processing of the cell culture. The CQDs are well fixed in the organelles of the cell even after its death; hence, this is a simple manner to keep the cell information for prolonged periods of time. Moreover, the integrated photostability of the CQDs internalized in in vitro cells is measured and it remains almost constant during at least 2 h, revealing their outstanding performance as fluorescent labels.

This article explores upscaling productivity of laser-generated nanoparticles in liquid and its automatization for industrial applications, considering laser and chamber design, scanner technology, liquid and target properties.

Research on Laser Powder Bed Fusion (L-PBF) of polymer powder feedstocks has raised over the last decade due to the increased utilization of the fabricated parts in aerospace, automotive, electronics, and healthcare applications. A total of 600 Science Citation Indexed articles were published on the topic of L-PBF of polymer powder feedstocks in the last decade, being cited more than 10,000 times leading to an h-index of 46. This study statistically evaluates the 100 most cited articles to extract reported material, process, and as-built part properties to analyze the research trends. PA12, PEEK, and TPU are the most employed polymer powder feedstocks, while size, flowability, and thermal behavior are the standardly reported material properties. Likewise, process properties such as laser power, scanning speed, hatch spacing, powder layer thickness, volumetric energy density, and areal energy density are extracted and evaluated. In addition, material and process properties of the as-built parts such as tensile test, flexural test, and volumetric porosity contents are analyzed. The incorporation of additives is found to be an effective route to enhance mechanical and functional properties. Carbon-based additives are typically employed in applications where mechanical properties are essential. Carbon fibers, Ca-phosphates, and SiO₂ are the most reported additives in the evaluated SCI-expanded articles for L-PBF of polymer powder feedstocks. A comprehensive data matrix is extracted from the evaluated SCI-index publications, and a principal component analysis (PCA) is performed to explore correlations between reported material, process, and as-built parts.

We present a novel route for the adsorption of pulsed laser-dispersed nanoparticles onto metal powders in aqueous solution without using any binders or surfactants. By electrostatic interaction, we deposit Y ₂ O ₃ nanoparticles onto iron–chromium based powders and obtain a high dispersion of nano-sized particles on the metallic powders. Within the additively manufactured component, we show that the particle spacing of the oxide inclusion can be adjusted by the initial mass fraction of the adsorbed Y ₂ O ₃ particles on the micropowder. Thus, our procedure constitutes a robust route for additive manufacturing of oxide dispersion-strengthened alloys via oxide nanoparticles supported on steel micropowders.