In this work, a novel red-emitting oxyfluoride phosphor Na₂NbOF₅:Mn⁴⁺ with an ultra-intense zero-phonon line (ZPL) was successfully synthesized by hydrothermal method. The phase composition and luminescent properties of Na₂NbOF₅:Mn⁴⁺ were studied in detail. The photoluminescence excitation spectrum contains two intense excitation bands centered at 369 and 470 nm, which match well with commercial UV and blue light-emitting diode (LED) chips. When excited by 470 nm blue light, Na₂NbOF₅:Mn⁴⁺ exhibits red light emission dominated by ZPL. Notably, the color purity of the Na₂NbOF₅:Mn⁴⁺ red phosphor can reach 99.9%. Meanwhile, the Na₂NbOF₅:Mn⁴⁺ phosphor has a shorter fluorescence decay time than commercial K₂SiF₆:Mn⁴⁺, which is conducive to fast switching of images in display applications. Profiting from the intense ZPL, white light-emitting diode (WLED) with high color rendering index of Ra = 86.2 and low correlated color temperature of T_c = 3133 K is realized using yellow YAG:Ce³⁺ and red Na₂NbOF₅:Mn⁴⁺ phosphor. The WLED fabricated using CsPbBr₃ quantum dots (QDs) and red Na₂NbOF₅:Mn⁴⁺ phosphor shows a wide color gamut of 127.56% NTSC (National Television Standard Committee). The results show that red-emitting Na₂NbOF₅:Mn⁴⁺ phosphor has potential application prospects in WLED lighting and display backlight.

A new green light-emitting phosphor with a PLQY of 70% was prepared by doping Cu⁺ into Cs₂MnCl₄. The WLED packaged by mixing commercial red and blue phosphors with Cs₂MnCl₄:0.1Cu⁺, exhibits a high CRI (R_a = 93) and low CCT (4080 K).