Biomaterials based on polyelectrolyte complexation are an innovative concept of coatings and packaging production to be applied in a wide range of food products. The aim of this study was to obtain and characterize a sodium alginate–chitosan complex material with variable degree of polyion interactions by complexation of oppositely charged polysaccharides. In order to characterize polyelectrolyte complexes, theromogravimetric analysis (TGA), dynamic mechanical thermal analysis (DMTA), nuclear magnetic resonance (NMR), Fourier transform infrared spectroscopy (FT-IR), matrix-assisted laser desorption/ionization technique with time of flight analyzer (MALDI-TOF), and scanning electron microscopy (SEM) were performed. TGA analysis showed that thermal decomposition temperature depends on the polymer ratio (R) and thermal resistance of samples was improved by increasing chitosan dosage. Accordingly to DMTA results, polyelectrolyte complexation led to obtain more flexible and resistant to mechanical deformation materials. Comparative analysis of the FTIR spectra of single polyelectrolytes, chitosan and alginate, and their mixtures indicated the formation of the polyelectrolyte complex without addition of reinforcing substances. MALDI-TOF analysis confirms the creation of polyelectrolyte aggregates (~197 Da) in samples with R ≥ 0.8; and their chemical stability and safety were proven by NMR analysis. The higher R the greater the number of polyanion–polycation aggregates seen in SEM as film morphology roughness.

The aim of the study was to obtain alginate oligosaccharides by using two degradation methods of sodium alginate (SA): with hydrochloric acid (G—guluronate, M—mannuronate and G + M fractions) and hydrogen peroxide (HAS—hydrolyzed SA), in order to assess and compare their biological activity and physico-chemical properties, with an attempt to produce gels from the obtained hydrolysates. The efficiency of each method was determined in order to select the fastest and most efficient process. The ferric ion reducing antioxidant power (FRAP), the ability to scavenge DPPH free radicals, rheological properties, Fourier Transformed Spectroscopy (FTIR) and the microbiological test against Escherichia coli and Staphylococcus aureus were performed. In order to check the functional properties of the obtained oligosaccharides, the texture profile analysis was assessed. The hydrolysis yield of acid SA depolymerization was 28.1% and from hydrogen peroxide SA, depolymerization was 87%. The FTIR analysis confirmed the degradation process by both tested methods in the fingerprint region. The highest ferric reducing antioxidant power was noted for HSA (34.7 µg), and the highest hydroxyl radical scavenging activity was obtained by G fraction (346 µg/Trolox ml). The complete growth inhibition (OD = 0) of alginate hydrolysates was 1%. All tested samples presented pseudoplastic behavior, only HSA presented the ability to form gel.

The aim of the study was to investigate the effect of using direct electric current (DC) of 0, 200, and 400 mA for five minutes on the physiochemical properties, cytotoxicity, antibacterial, and antioxidant activity of sodium alginate hydrosols with different sodium chloride concentrations. The pH, oxidation-reduction potential (ORP), electrical conductivity (EC), and available chlorine concentration (ACC) were measured. The effect of sodium alginate hydrosols treated with DC on Staphylococcus aureus, Listeria monocytogenes, Bacillus cereus, Micrococcus luteus, Escherichia coli, Salmonella enteritidis, Yersinia enterocolitica, Pseudomonas fluorescence, and RAW 264.7 and L929 cells was investigated. Subsequently, the antioxidant properties of hydrosols were evaluated by determining the scavenging ability of 1,1-diphenyl-2-picrylhydrazyl free radical (DPPH) and ferric reducing antioxidant power (FRAP). The results have shown that after applying 400 mA in hydrosol samples with 0.1% and 0.2% NaCl all tested bacteria were inactivated. The ACC concentration of C400 samples with NaCl was equal to 13.95 and 19.71 mg/L, respectively. The cytotoxicity analysis revealed that optimized electric field conditions and the addition of sodium chloride allow for the avoidance of toxicity effects on normal cells without disturbing the antibacterial effects. Due to the presence of oxidizing substances, the DPPH of variants treated with DC was lower than the DPPH of control samples.

Meat is one of the most challenging food products in the context of maintaining quality and safety. The aim of this work was to improve the quality of raw/cooked meat by coating it with sodium alginate (A), chitosan (C), and sodium alginate-chitosan polyelectrolyte complex (PEC) hydrosols. Antioxidant properties of A, C, and PEC hydrosols were determined. Subsequently, total antioxidant capacity (TAC), sensory quality of raw/cooked pork coated with experimental hydrosols, and antimicrobial efficiency of those hydrosols on the surface microbiota were analysed. Application analyses of hydrosol were performed during 0, 7, and 14 days of refrigerated storage in MAP (modified atmosphere packaging). Ferric reducing antioxidant power (FRAP) and (2,2-diphenyll-picrylhydrazyl (DPPH) analysis confirmed the antioxidant properties of A, C, and PEC. Sample C (1.0%) was characterized by the highest DPPH value (174.67 μM Trolox/mL) of all variants. PEC samples consisted of A 0.3%/C 1.0% and A 0.6%/C 1.0% were characterized by the greatest FRAP value (~7.21 μM Fe²⁺/mL) of all variants. TAC losses caused by thermal treatment of meat were reduced by 45% by coating meat with experimental hydrosols. Application of PEC on the meat surface resulted in reducing the total number of micro-organisms, psychrotrophs, and lactic acid bacteria by about 61%, and yeast and molds by about 45% compared to control after a two-week storage.

The aims of this study were to obtain chitooligosaccharides (COS) from chitosan (CH) with improved functional properties and comparison of the use of two different enzymes: commercial cellulase (CL) and the dedicated enzyme chitosanase (CS). After enzymatic reaction, chitosan oligomers (NFs) were isolated by methanol into two fractions: precipitate (HMF) and supernatant (LMF). The occurrence of a hydrolysis reaction was confirmed by an increased reducing sugar content and viscosity reduction of chitosan oligomers. CPMAS ¹³C NMR analysis confirmed the dissimilar cleavage mechanism of the enzymes used. LMF and NF fractions were characterised by improved solubility in water (94.56%) compared to the HMF and CH samples (70.64%). Thermogravimetric analysis (TGA) showed that the HMF decomposed in two-stage process while CH, NF, and LMF decomposed in a three-stage process. The greatest mass loss of LMF samples (58.35%) suggests their sensitivity to high-temperature treatments. COS were a mixture of DP (degrees of polymerisation) from 3 to 18 hetero-chitooligomers, with an average Mw of NF > HMF > CH.