Parts made from thermoplastic polymers fabricated through 3D printing have reduced mechanical properties compared to those fabricated through injection molding. This paper analyzes a post-processing heat treatment aimed at enhancing mechanical properties of 3D printed parts, in order to reduce the difference mentioned above and thus increase their applicability in functional applications. Polyethylene Terephthalate Glycol (PETG) polymer is used to 3D print test parts with 100% infill. After printing, samples are packed in sodium chloride powder and then heat treated at a temperature of 220 °C for 5 to 15 min. During heat treatment, the powder acts as support, preventing deformation of the parts. Results of destructive testing experiments show a significant increase in tensile and compressive strength following heat treatment. Treated parts 3D printed in vertical orientation, usually the weakest, display 143% higher tensile strength compared to a control group, surpassing the tensile strength of untreated parts printed in horizontal orientation—usually the strongest. Furthermore, compressive strength increases by 50% following heat treatment compared to control group. SEM analysis reveals improved internal structure after heat treatment. These results show that the investigated heat treatment increases mechanical characteristics of 3D printed PETG parts, without the downside of severe part deformation, thus reducing the performance gap between 3D printing and injection molding when using common polymers.

In the context of the COVID-19 pandemic, shortwave ultraviolet radiation with wavelengths between 200 nm and 280 nm (UV-C) is seeing increased usage in the sterilization of medical equipment, appliances, and spaces due to its antimicrobial effect. During the first weeks of the pandemic, healthcare facilities experienced a shortage of personal protective equipment. This led to hospital technicians, private companies, and even members of the public to resort to 3D printing in order to produce fast, on-demand resources. This paper analyzes the effect of accelerated aging through prolonged exposure to UV-C on mechanical properties of parts 3D printed by material extrusion (MEX) from common polymers, such as polylactic acid (PLA) and polyethylene terephthalate-glycol (PETG). Samples 3D printed from these materials went through a 24-h UV-C exposure aging cycle and were then tested versus a control group for changes in mechanical properties. Both tensile and compressive strength were determined, as well as changes in material creep properties. Prolonged UV-C exposure reduced the mechanical properties of PLA by 6–8% and of PETG by over 30%. These findings are of practical importance for those interested in producing functional MEX parts intended to be sterilized using UV-C. Scanning electron microscopy (SEM) was performed in order to assess any changes in material structure.

In outdoor environments, the action of the Sun through its ultraviolet radiation has a degrading effect on most materials, with polymers being among those affected. In the past few years, 3D printing has seen an increased usage in fabricating parts for functional applications, including parts destined for outdoor use. This paper analyzes the effect of accelerated aging through prolonged exposure to UV-B on the mechanical properties of parts 3D printed from the commonly used polymers polylactic acid (PLA) and polyethylene terephthalate–glycol (PETG). Samples 3D printed from these materials went through a dry 24 h UV-B exposure aging treatment and were then tested against a control group for changes in mechanical properties. Both the tensile and compressive strengths were determined, as well as changes in material creep characteristics. After irradiation, PLA and PETG parts saw significant decreases in both tensile strength (PLA: −5.3%; PETG: −36%) and compression strength (PLA: −6.3%; PETG: −38.3%). Part stiffness did not change significantly following the UV-B exposure and creep behavior was closely connected to the decrease in mechanical properties. A scanning electron microscopy (SEM) fractographic analysis was carried out to better understand the failure mechanism and material structural changes in tensile loaded, accelerated aged parts.

This research investigates the tensile strength and microstructural properties of stainless steel 316L, comparing samples fabricated using additive manufacturing (AM) to those produced via conventional manufacturing techniques such as forging and casting using stainless steel 316L for its mechanical performance and corrosion resistance. Tensile tests revealed that AM samples had an ultimate tensile strength (UTS) of 650 MPa, a yield strength of 550 MPa and an elongation at break of 20%, and conventionally manufactured samples achieved a UTS of 580 MPa, a yield strength of 450 MPa and a higher elongation at break of 35%. The reduced ductility of AM samples is offset by their higher strength. Scanning electron microscopy (SEM) analysis showed that AM samples had a refined grain structure, with grain sizes ranging from 1 to 5 µm, whereas conventionally produced samples exhibited larger grain sizes of 10 to 20 µm, contributing to their increased ductility. This shows that while AM processes can give a rather high strength, the ductility property is simpler to attain with casting. Further work is needed to investigate post-processing techniques like hot isotropic pressing (HIP) and heat treatments for enhancing the ductility of AM parts as well as mechanical properties.