In this study, new biodegradable and biocompatible amphiphilic polymers were obtained by modifying the peripheral hydroxyl groups of branched polyethers and polyesters with organosilicon substituents. The structures of the synthesized polymers were confirmed by NMR and GPC. Organosilicon moieties of the polymers were formed by silatranes and trimethylsilyl blocks and displayed hydrophilic and hydrophobic properties, respectively. The effect of the ratio of hydrophilic to hydrophobic organosilicon structures on the surface activity and biological activity of macromolecules was studied, together with the effect on these activities of the macromolecules’ molecular weight and chemical structure. In particular, the critical micelle concentrations were determined, the effect of the structure of the polymers on their wetting with aqueous solutions on glass and parafilm was described, and the aggregation stability of emulsions was studied. Finally, the effect of the polymer structures on their antifungal activity and seed germination stimulation was examined.

The combination of biocompatibility, biodegradability, and high mechanical strength has provided a steady growth in interest in the synthesis and application of lactic acid-based polyesters for the creation of implants. On the other hand, the hydrophobicity of polylactide limits the possibilities of its use in biomedical fields. The ring-opening polymerization of L-lactide, catalyzed by tin (II) 2-ethylhexanoate in the presence of 2,2-bis(hydroxymethyl)propionic acid, and an ester of polyethylene glycol monomethyl ester and 2,2-bis(hydroxymethyl)propionic acid accompanied by the introduction of a pool of hydrophilic groups, that reduce the contact angle, were considered. The structures of the synthesized amphiphilic branched pegylated copolylactides were characterized by ¹H NMR spectroscopy and gel permeation chromatography. The resulting amphiphilic copolylactides, with a narrow MWD (1.14–1.22) and molecular weight of 5000–13,000, were used to prepare interpolymer mixtures with PLLA. Already, with the introduction of 10 wt% branched pegylated copolylactides, PLLA-based films had reduced brittleness, hydrophilicity, with a water contact angle of 71.9–88.5°, and increased water absorption. An additional decrease in the water contact angle, of 66.1°, was achieved by filling the mixed polylactide films with 20 wt% hydroxyapatite, which also led to a moderate decrease in strength and ultimate tensile elongation. At the same time, the PLLA modification did not have a significant effect on the melting point and the glass transition temperature; however, the filling with hydroxyapatite increased the thermal stability.

Linear-hyperbranched co(polylactides) containing hyperbranched polyglycerol (PG) block were synthesized and characterized. An estimate of critical micelle concentration as well as aggregative stability and droplet sizes in the emulsion stabilized by the obtained polymers was made. It was shown that an architecture of linear-branched co(polylactides) defines its surface-active properties and characteristics of dispersion systems obtained from it. With an increase in PG block content in copolymers, critical micelle concentration and aggregative stability of emulsions increase. Polylactide microparticles were obtained by organic solvent evaporation technique using acetylsalicylic acid as a drug model. Some properties of microparticles, such as size, incorporation efficiency and in vitro release of immobilized substance, were examined. It was noticed that branching architecture of co(polylactides) has a significant influence on the properties of microparticles. On the one hand, the presence of large PG blocks in linear-branched macromolecules results in the formation of colloidal systems with higher aggregative stability of emulsions and smaller particle size; on the other hand, microparticles formed from such copolymers have lower incorporation efficiency towards water-soluble low-molecular-weight compounds and nonlinear release profile for these substances with a segment of accelerated primary release.

Various hydroxyapatite-filled and unfilled microspheres based on lactide and glycolide copolymers were prepared. The synthesized poly(lactic-co-glycolic acid) (PLGA) samples were characterized by GPC and ¹H NMR spectroscopy, the morphology was characterized by SEM. It was shown that under the tin (II) 2-ethylhexanoate catalysis the glycolide is highly active in copolymerization as compared with lactide. According to the data on weight loss and the weight average molecular weight shift of PLGA over time (pH = 6.5; t = 25 °C), an increase in the rate of microsphere destruction was noted when macromolecules were enriched with glycolic acid residues, as well as when filled with hydroxyapatite. It was shown that the rate of PLGA degradation was determined by the water-accessible surface of a sample. The rate increase in PLGA hydrolytic degradation both with an increase in glycolic acid residues mole fraction in the chain and upon filling with hydroxyapatite was the result of the microspheres’ surface hydrophilization, an increase in capillary pressure upon filling of the pores as well as of the defects with water, and an increase in the number of structural defects. Approaches to the creation of composite microspheres based on PLGA degrading at a controlled rate were proposed.