Thermal modification is a well-established commercial technology for improving the dimensional stability and durability of timber. Numerous reviews of thermally modified timber (TMT) are to be found in the scientific literature, but until now a review of the influence of cell wall moisture content during the modification process on the properties of TMT has been lacking. This paper reviews the current state of knowledge regarding the hygroscopic and dimensional behaviour of TMT modified under dry (cell wall at nearly zero moisture content) and wet (cell wall contains moisture) conditions. After an overview of the topic area, the review explores the literature on the thermal degradation of the polysaccharidic and lignin components of the cell wall, as well as the role of extractives. The properties of TMT modified under wet and dry conditions are compared including mass loss, hygroscopic behaviour and dimensional stability. The role of hydroxyl groups in determining the hygroscopicity is discussed, as well as the importance of considering the mobility of the cell wall polymers and crosslinking when interpreting sorption behaviour. TMT produced under wet processing conditions exhibits behaviour that changes when the wood is subjected to water leaching post-treatment, which includes further weight loss, changes in sorption behaviour and dimensional stability, but without any further change in accessible hydroxyl (OH) content. This raises serious questions regarding the role that OH groups play in sorption behaviour.Graphical

This paper reviews the degradation, preservation and conservation of waterlogged archaeological wood. Degradation due to bacteria in anoxic and soft-rot fungi and bacteria in oxic waterlogged conditions is discussed with consideration of the effect on the chemical composition of wood, as well as the deposition of sulphur and iron within the structure. The effects on physical properties are also considered. The paper then discusses the role of consolidants in preserving waterlogged archaeological wood after it is excavated as well as issues to be considered when reburial is used as a means of preservation. The use of alum and polyethylene glycol (PEG) as consolidants is presented along with various case studies with particular emphasis on marine artefacts. The properties of consolidated wood are examined, especially with respect to the degradation of the wood post-conservation. Different consolidants are reviewed along with their use and properties. The merits and risks of reburial and in situ preservation are considered as an alternative to conservation.

The aim of this research is to determine if the polyesterification of sorbitol and citric acid in wood has a future potential as a wood modification process. Pine wood was impregnated with an aqueous solution containing citric acid and sorbitol and was thereafter cured at 103 or 140°C for 18 hours. The dimensional stability and leaching resistance were studied for both modification temperatures. The leachates from the modified wood samples were analysed by HPLC and the susceptibility to decay and staining fungi were studied. Impregnated samples cured at 140°C showed a permanent (leach-resistant) increased dimensional change, but samples treated at 103°C were not stable to leaching. Treated samples cured at 103 and 140°C showed significant resistance to white-rot (Trametes versicolor) and brown-rot decay (Postia placenta) after a leaching procedure. Furthermore, samples cured at 103 and 140°C (leached and unleached) were significantly less susceptible to blue-stain fungi than the untreated controls.

Timber cladding has been used since historical times as a locally available, affordable weather protection option. Nowadays, interest in timber cladding is again increasing because of ecological reasons as well as naturalistic viewpoints. This review presents a comprehensive report on timber cladding in a European context, beginning with a brief overview of the history before considering contemporary use of timber cladding for building envelopes. The basic principles of good design are considered, paying attention to timber orientation, fixings and environmental risk factors. The relationship of timber with moisture is discussed with respect to sorption behaviour, dimensional instability and design methods to minimise the negative consequences associated with wetting. The behaviour of timber cladding in fires, the effects of environmental stresses and weathering, as well as the cladding properties and the variation thereof with different types of wood and anatomical factors (including exposure of different timber faces), are examined. The review then moves on to considering different methods for protecting timber, such as the use of coatings, preservatives, fire retardants and wood modification. A brief discussion of various environmental considerations is also included, including life cycle assessment, embodied carbon and sequestered atmospheric carbon. The review finishes by making concluding remarks, providing a basis for the selection of appropriate cladding types for different environments.

Acetylated wood (W_Ac) shows improved properties largely due to the reduced amount of water in its cell wall, but the exact mechanism of water reduction remains unclear. Acetylation reduces hydroxyl (OH) content by acetyl (Ac) substitution but may also limit water access to unmodified OH groups by steric hindrance. In the present work, the accessibility of OH groups in acetylated or propionylated Radiata pine (Pinus radiata D. Don) wood (W_Ac and W_Pr) was investigated by deuterium exchange, saponification in sodium hydroxide followed by high-performance liquid chromatography (HPLC) analysis and weight percentage gain determination of the modified samples. Acetylation reduced OH accessibility (OH_A) to a greater extent than would be predicted, if OH substitution were the only responsible mechanism for accessibility reduction. The combination of deuterium exchange and saponification results provides strong evidence that steric hindrance plays a key role in reduction of water accessibility to unmodified OH groups in W_Ac. The supramolecular architecture of W_Pr samples seems to be modified by the propionylation reaction, which leads to increased OH_A at low levels of substitution. This suggests that molecular restructuring within the cell wall exposes new OH groups after propionylation. At higher levels of substitution, however, the W_Pr exhibited less OH_A than expected indicating steric hindrance from the propionyl groups.