In this research, iron ore tailing (IOT) is utilized as the cementitious material to develop an eco-friendly ultra-high performance concrete (UHPC). The UHPC mix is obtained according to the modified Andreasen and Andersen (MAA) packing model, and the applied dosage of IOT is 10%, 20%, and 30% (by weight), respectively. The calculated packing density of different mixtures is consistent with each other. Afterwards, the fresh and hardened performance of UHPC mixtures with IOT are evaluated. The results demonstrate that the workability of designed UHPC mixtures is increased with the incorporation of IOT. The heat flow at an early age of designed UHPC with IOT is attenuated, the compressive strength and auto shrinkage at an early age are consequently reduced. The addition of IOT promotes the development of long-term compressive strength and optimization of the pore structure, thus the durability of designed UHPC is still guaranteed. In addition, the ecological estimate results show that the utilization of IOT for the UHPC design can reduce the carbon emission significantly.

The suitability of applying shrinkage reducing additives in alkali activated coal gangue-slag composites is discussed in this study. The effect of sulphoaluminate cement (SAC), high performance concrete expansion agent (HCSA) and U-type expansion agent (UEA) on the reaction process, shrinkage behavior, phase composition, microstructure and mechanical properties are evaluated. The results show that the addition of SAC slightly mitigates the early stage reaction process, while HCSA and UEA can either accelerate or inhibit the reaction depending on their dosage. The addition of SAC presents an ideal balance between drying shrinkage reduction and strength increment. As for HCSA and UEA, the shrinkage and mechanical properties are sensitive to their replacement level; excessive dosage would result in remarkable strength reduction and expansion. The specific surface area and average pore size of the hardened matrix are found to be closely related with shrinkage behavior. SAC addition introduces additional hydrotalcite phases within the reaction products, while HCSA and UEA mainly result in the formation of CaCO₃ and Ca(OH)₂. It is concluded that applying expansive additives can be an effective approach in reducing the drying shrinkage of alkali activated coal gangue-slag mixtures, while their type and dosage must be carefully handled.

The application of polymer latex provides an additional approach when optimizing the properties of high–performance cement–based materials. Given that cement–based materials are extraordinarily sensitive to the characteristics and relative content of polymer latexes, identifying their influence is essential for application. This paper investigates the impact of polymer latex types and its relative content on the mechanical properties, hydration product, pore structure, and drying shrinkage of cement–based materials with a low water to binder ratio. The results showed that the mechanical properties, pore structure, and drying shrinkage of the styrene butadiene latex modified samples were better than those of ethylene vinyl acetate latex and silicone acrylic latex modified ones. Incremental increases to the polymer to cement ratio induces a slight reduction on compressive strength, and styrene–butadiene latex promotes tensile strength. Polymer latex hinders the transformation from ettringite to monosulfate, reducing the bound water and portlandite generated. Increasing the polymer content induces more significant stretching in the vibration peak of SO₄ from ettringite. Further incorporation of polymer latex contributes to ettringite precipitation and the decline of harmful pores. Polymer addition also results in lower drying shrinkage compared with the reference group.

For solid waste-based cementitious materials, most scholars focus their research on the hydration reaction of cementitious materials, but there is still a lack of solid waste design that comprehensively considers mechanical properties and durability. Therefore, this article focuses on exploring the mix of design and the microscopic and macroscopic properties of multi solid waste cementitious materials (MSWCMs), namely steel slag (SS), slag powder (SP), desulfurization gypsum (DG), fly ash (FA), and ordinary Portland cement (OPC). According to the orthogonal experimental results, the compressive strength of MSWCMs is optimal when the OPC content is 50% and the SS, SP, DG, and FA contents are 10%, 20%, 5%, and 15%, respectively. The MSWCMs group with an OPC content of 50% and SS, SP, DG, and FA contents of 5%, 15%, 5%, and 25% was selected as the control group. The pure OPC group was used as the blank group, and the optimal MSWCMs ratio group had a 28-day compressive strength of 50.7 megapascals, which was 14% and 7.6% higher than the control group and blank group, respectively. The drying shrinkage rate and resistance to chloride ions were also significantly improved, with maximum increases of 22.9%, 22.6%, and 8.9%, 9.8%, respectively. According to XRD, TG-DTG, and NMR testing, the improvement in macroscopic performance can be attributed to the synergistic effect between various solid wastes. This synergistic effect produces more ettringite (AFt) and C-(A)-S-H gel. This study provides a good theoretical basis for improving the comprehensive performance of MSWCMs and is conducive to reducing the use of cement, with significant economic and environmental benefits.

Microwave heating is an effective method to achieve autonomic crack healing in asphalt mixtures, and the use of microwave-absorbing materials can largely improve this healing efficiency. As a solid waste, coal gangue contains metal oxides, which shows the possibility of microwave heating. In order to further promote the application of coal gangue in the microwave healing of asphalt mixtures, this study looks into the synergistic effect of basalt and coal gangue powder (CGP) on the microwave heating self-healing of an asphalt mixture. The mechanical performance, water stability, low-temperature crack resistance and microwave healing efficiency of the asphalt mixture were investigated using the immersion Marshall test, standard Marshall test, Cantabro test and semi-circular bending (SCB), and healing tests, respectively. The results indicated that the addition of CGP in asphalt mixture can improve the microwave heating speed, which also showed a significant advantage in water stability and fracture energy recovery. The research results will further promote the utilization rate of coal gangue.

In this study, rubberized cementitious materials are produced with recycled rubber waste as an alternative to fine aggregate. Mixtures with different additions to rubber wastes (RW), silica fume (SF), and blast furnace slag (BFS) have been designed and characterized. Hardened properties including compressive and bond strength, shrinkage, water-accessible porosity, rapid chloride migration, and microstructure were investigated. The results show that the addition of SF and BFS improves the performances of rubberized mortars and reduces shrinkage. The incorporation of 5% RW with 20% BFS increases compressive strength and reduces water-accessible porosity. Ion chloride resistance was enhanced by a combination of 15% RW, 8% SF, and 20% BFS. The addition of SF and BFS as cement replacement improves the performance of mortars due to their filling effect and a pozzolanic reaction, which has been verified by a microstructural analysis.