Nanocomposites comprising high-density polyethylene (HDPE) and boehmite (BA) nanoparticles were prepared by melt blending and subsequently irradiated with electrons. Electron irradiation of HDPE causes crosslinking and, in the presence of BA, generates ketone functional groups. The functional groups can then form hydrogen bonds with the hydroxyl groups on the surface of the BA. Additionally, if the BA is surface modified by vinyltrimethoxysilane (vBA), it can covalently bond with the HDPE by irradiation-induced radical grafting. The strong covalent bonds generated by electron beam irradiation allow the desirable properties of the nanofiller to be transferred to the rest of the nanocomposite. Since EB irradiation produces a great number of strong covalent bonds between vBA nanoparticles and HDPE, the modulus of elasticity, yield strength, and resistance to thermal shrinkage are enhanced by electron irradiation.

The effect of scintillator particle size on high-resolution X-ray imaging was studied using zinc tungstate (ZnWO₄) particles. The ZnWO₄ particles were fabricated through a solid-state reaction between zinc oxide and tungsten oxide at various temperatures, producing particles with average sizes of 176.4 nm, 626.7 nm, and 2.127 μm; the zinc oxide and tungsten oxide were created using anodization. The spatial resolutions of high-resolution X-ray images, obtained from utilizing the fabricated particles, were determined: particles with the average size of 176.4 nm produced the highest spatial resolution. The results demonstrate that high spatial resolution can be obtained from ZnWO₄ nanoparticle scintillators that minimize optical diffusion by having a particle size that is smaller than the emission wavelength.