In this study, bamboo charcoal (BC) was used as a substitute filler for bamboo powder (BP) in a lignocellulose-plastic composite made from polylactic acid (PLA), with aluminum hypophosphite (AHP) added as a fire retardant. A set of BC/PLA/AHP composites were successfully prepared and tested for flame-retardancy properties. Objectives were to (a) assess compatibility and dispersibility of BC and AHP fillers in PLA matrix, and (b) improve flame-retardant properties of PLA composite. BC reduced flexural properties while co-addition of AHP enhanced bonding between PLA and BC, improving strength and ductility properties. Adding AHP drastically reduced the heat release rate and total heat release of the composites by 72.2% compared with pure PLA. The formation of carbonized surface layers in the BC/PLA/AHP composites effectively improved the fire performance index (FPI) and reduced the fire growth index (FGI). Flame-retardant performance was significantly improved with limiting oxygen index (LOI) of BC/PLA/AHP composite increased to 31 vol%, providing a V-0 rating in UL-94 vertical flame test. Adding AHP promoted earlier initial thermal degradation of the surface of BC/PLA/AHP composites with a carbon residue rate up to 40.3%, providing a protective layer of char. Further raw material and char residue analysis are presented in Part II of this series.

A cooperative flame-retardant system based on natural intumescent-grafted bamboo charcoal (BC) and chitosan (CS) was developed for polylactic acid (PLA) with improved flame retardancy and minimal decline in strength properties. Chitosan (CS) as an adhesion promoter improved the interfacial compatibility between graft-modified bamboo charcoal (BC-m) and PLA leading to enhanced tensile properties by 11.11% and 8.42%, respectively for tensile strength and modulus. At 3 wt.% CS and 30 wt.% BC-m, the crystallinity of the composite increased to 38.92%, or 43 times that of pure PLA (0.9%). CS promotes the reorganization of the internal crystal structure. Thermogravimetric analysis showed significantly improved material retention of PLA composites in nitrogen and air atmosphere. Residue rate for 5 wt.% CS and 30 wt.% BC-m was 29.42% which is 55.1% higher than the theoretical value of 18.97%. Flammability tests (limiting oxygen index-LOI and UL-94) indicated significantly improved flame retardancy and evidence of cooperation between CS and BC-m, with calculated cooperative effectiveness index(Ce) >1. From CONE tests, the peak heat release rate (pHRR) and total heat release (THR) were reduced by 26.9% and 30.5%, respectively, for 3% CS + 20% BC-m in PLA compared with adding 20% BC-m alone. Analysis of carbon residue morphology, chemical elements and structure suggest CS and BC-m form a more stable char containing pyrophosphate. This char provides heat insulation to inhibit complete polymer pyrolysis, resulting in improved flame retardancy of PLA composites. Optimal mix may be recommended at 20% BC-m + 3% CS to balance compatibility, composite strength properties and flame retardance.

Controlling the variability in mat structure and properties in bamboo scrimber (BS) is key to producing the product for structural applications, and wide strip scrimber (WBS) is an effective approach. In this study, the effects of scrimmed bamboo bundle morphology and product density on the properties of WBS were investigated. WBS panels were manufactured and tested using wide (200 to 250 mm) bamboo strips with different fiberization intensity. Maximum strength properties (flexural, compressive, and shear strength), and lowest thickness swelling and water absorption were achieved with three or four passes due to the higher resin absorption by strips. For balanced product cost and performance, we recommend 1–2 fiberization passes and a panel density of 0.9–1.0 g/cm³. Panel mechanical properties were compared with other common bamboo composites. Bamboo scrimber products were highly variable in properties due to differing manufacturing processes, element treatments, and suboptimal mat structure. Products including laminated bamboo lumber and flattened bamboo made from nonfiberized elements show markedly different relationships between strength and elastic properties mostly due to inadequate bonding between the laminae, which causes premature bond-line failure. This study helped improve the understanding of the structure–property relationship of engineered bamboo products while providing insights into process optimization.

Bamboo charcoal (BC) and aluminum hypophosphite (AHP) singly and in combination were investigated as flame-retardant fillers for polylactic acid (PLA). A set of BC/PLA/AHP composites were prepared by melt-blending and tested for thermal and flame-retardancy properties in Part I. Here, in Part II, the results for differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Fourier transform infrared (FTIR), thermogravimetry-Fourier transform infrared spectrometry (TG-FTIR), X-ray diffraction (XRD), and X-ray photoelectron analysis (XPS) are presented. The fillers either singly or together promoted earlier initial thermal degradation of the surface of BC/PLA/AHP composites, with a carbon residue rate up to 40.3%, providing a protective layer of char. Additionally, BC promotes heterogeneous nucleation of PLA, while AHP improves the mechanical properties and machinability. Gaseous combustion products CO, aromatic compounds, and carbonyl groups were significantly suppressed in only the BC-PLA composite, but not pure PLA or the BC/PLA/AHP system. The flame-retardant effects of AHP and BC-AHP co-addition combine effective gas-phase and condensed-phase surface phenomena that provide a heat and oxygen barrier, protecting the inner matrix. While it generated much CO₂ and smoke during combustion, it is not yet clear whether BC addition on its own contributes any significant gas phase protection for PLA.

Bamboo fiber composite (BFC) is a unidirectional and continuous bamboo fiber composite manufactured by consolidation and gluing of flattened, partially separated bamboo culm strips into thick and dense panels. The composite mechanical properties are primarily influenced by panel density, its variation and uniformity. This paper characterized the horizontal density distribution (HDD) within BFC panels and its controlling factors. It revealed that HDD follows a normal distribution, with its standard deviation (SD) strongly affected by sampling specimen size, panel thickness and panel locations. SD was lowest in the thickest (40 mm) panel and largest-size (150 × 150-mm²) specimens. There was also a systematic variation along the length of the BFC due to the tapering effect of bamboo culm thickness. Density was higher along panel edges due to restraint from the mold edges during hot pressing. The manual BFC mat forming process is presented and found to effectively minimize the density variation compared to machine-formed wood composites. This study provides a basic understanding of and a quality control guide to the formation uniformity of BFC products.

Understanding the maturation stress and wood properties of poplar tension wood is critical for improving lumber yields and utilization ratio. In this study, the released longitudinal maturation strains (RLMS), anatomical features, physical and mechanical properties, and nano-mechanical properties of the cell wall were analyzed at different peripheral positions and heights in nine artificially inclined, 12-year-old poplar (Populus × euramericana cv. ‘Zhonglin46’) trees. The correlations between the RLMS and the wood properties were determined. The results showed that there were mixed effects of inclination on wood quality and properties. The upper sides of inclined stems had higher RLMS, proportion of G-layer, bending modulus of elasticity, and indentation modulus of the cell wall but a lower microfibril angle than the lower sides. At heights between 0.7 m and 2.2 m, only the double-wall thickness increased with height; the RLMS and other wood properties such as fiber length and basic density fluctuated or changed little with height. The RLMS were good indicators of wood properties in the tension wood area and at heights between 0.7 m and 1.5 m. The results of this study present opportunities to better understand the interactions and effects of these two phenomena, which both occur quite frequently in poplar stands and can influence the wood quality of valuable assortments.