The main objective of this study was to evaluate the effect of functionalized silica nanoparticles with Fe₂O₃, NiO, and MoO₃ metal oxides on the decomposition of asphaltenes, through an experimental simplex–centroid mixture design for surface area, asphaltene adsorption, and activation energy. The experimental nanoparticle surface area was measured by adsorption of N₂. Adsorption isotherms, and the subsequent oxidation process of asphaltenes, were performed through batch adsorption experiments and thermogravimetric analysis, respectively. Among the monometallic systems, the presence of iron increased the affinity between the nanoparticle and the asphaltenes, and a higher metal oxide load increased the adsorptive capacity of the system. For the pairings evaluated, there was better synergy between iron and nickel, with the participation of the former being slightly superior. In the mixture design that included three transition elements, the participation of molybdenum was not significant, and the adsorption of asphaltenes was dominated by the active sites formed by the other two transition element oxides. The mixture design created to minimize the activation energy showed that the interaction of the three transition elements is important and can be evidenced in the interaction coefficients.

In this work several issues related to asphaltenes and asphaltene aggregates such as isolation of real asphaltene molecules and comparison of these with average structures obtained using regular analytics laboratory techniques are presented. Several molecular organic models were used to simulate asphaltene in solution and aggregates formation in the two solvents toluene and THF employed. The results, obtained from simulation calculations using molecular dynamics were compared with experimental chromatography results obtained using the micro gel permeation chromatography (μGPC), inductively coupled plasma (ICP) mass spectra (MS) combined technique (GPC ICP MS for short). In this case reasonable hydrodynamic ratios and size distribution were obtained for asphaltenes and their corresponding subfractions A1 and subfraction A2. Comparison between experimental sample profiles, transmission of electron microscopy (TEM) data, and molecular dynamics allows for estimation of hydrodynamic ratios of around 8 nm. Highly aromatic and island type molecular model A30 and continental type molecular model A40 were employed in the molecular dynamics to built colloids. In this case open-like colloids (A40) and compact-like colloids A30 were obtained. Subjects such as trapped compounds (TC), metallic porphyrins, and colloidal dipole moments were also studied. Studies of the adsorption behavior of asphaltenes on several macroscopic and nanoscopic surfaces are presented and show the tendency of the asphaltene to adsorb in aggregate form.