Background: Phosphorus-containing high performance polymers have aroused wide interest, mainly due to good mechanical properties and their excellent fire resistance. The flexibility of synthetic polyphosphoesters allows the development of polymers in order to obtain solid polymer electrolytes for rechargeable lithium batteries based on solid films with superior fire resistance. Results: Novel linear Phosphonate-PEG polymers were synthesized by solution polycondensation of 4-chlorophenyldichlorophosphonate as a linking agent and poly(ethylene glycol)s with different molecular weights in the presence of triethylamine or 1-methylimidazole as acid scavenger. The yields were between 54% and 88% and inherent viscosity between 0.18-0.48 dl/g. Molar masses, Mn were about 26300 g/mol for polyphosphonates with PEG 2000 and 4600 g/mol for polyphosphonates with PEG 200. The LOI values for these polymers and membranes are in the range of 26–29. The membranes based on polyphosphonate with PEG 200 and 2000 showed conductivity between 6 × 10^-8 S.cm^-1 and 6 × 10^-7 S.cm^-1 at room temperature and total ionic transference number between 0.87- 0.96. The evolution of conductivity vs. temperature is linear. Conclusions: 1-methylimidazole was found to be better HCl scavenger than triethylamine, and allowed higher yields and more eco-friendly synthesis of the Phosphonate-PEG polymers for SPE. These polymers and membranes based on these polymers showed good LOI values and indicate an improvement of the safety of lithium batteries. The membranes present conductivities around 6 × 10^-7 S.cm^-1at room temperature and total ionic transference number is higher for membranes based on polymers with high EG unit content. Best results yield 88%, inherent viscosities 0.48 dl/g and Mn 26000 were obtained with 1-methylimidazole and PEG 2000. These membranes based on these polymers showed good LOI values (in the range 26-29%) and indicate an improvement of the safety of lithium batteries.

The behavior of p-methoxybenzoyldiphenylphosphine oxide, previously synthesized, as a photoinitiator for the polymerization of diacrylate monomer, in the presence of 3% (w/w) tertiary amine (triethyl amine) as synergist additive, was studied. The influence of temperature in the range 30–90°C at 3% (w/w) photoinitiator concentration and the influence of the photoinitiator concentration in the range 0.5–3.5% (w/w) at 30°C was investigated by differential scanning photocalorimetry (photo-DSC). In all experiments the photopolymerization was performed at constant light intensity (3 mW cm⁻²). The maximum conversion was obtained at temperature of 90°C at 3% (w/w) photoinitiator concentration and 3% (w/w) triethyl amine. The optimal concentration of photoinitiator to obtain maximum conversion was 3% (w/w), at 30°C. No thermal polymerization occurred at higher temperature.

This paper is directed towards the development of safe, and thermally stable solid polymer electrolytes. Linear phosphorus-containing (co)polyesters are described, including their synthesis, thermal analysis, conductivity, and non-flammability. Polycondensation of phenylphosphonic dichloride (PPD) with poly(ethylene glycol) (PEG 12000) with and without bisphenol A (BA) was carried out using solid-liquid phase transfer catalysis. Potassium phosphate is used as base. Yields in the range of 85.0–88.0%, and inherent viscosities in the range of 0.32–0.58 dL/g were obtained. The polymers were characterized by gel permeation chromatography, FT-IR, ¹H- and ³¹P-NMR spectroscopy and thermal analysis. Their flammability was investigated by measuring limiting oxygen index values. The polymers are flame retardants and begin to lose weight in the 190 °C–231 °C range. Solid phosphorus- containing (co)polyesters were complexed with lithium triflate and the resulting ionic conductivity was determined. Conductivities in the range of 10⁻⁷–10⁻⁸ S cm⁻¹ were obtained.

Organophosphorus chemistry was developed in the last decade by promoting the synthesis reactions using ionic liquids either as solvent or catalyst. Ionic liquids (ILs), the so-called “green solvents”, have gained interest in the synthesis of organophosphorus compounds as alternatives to flammable and toxic organic solvents and catalysts. ILs have beneficial properties because they provide high solubility for many organic and inorganic compounds or metal complexes, have no vapor pressure, and are reusable. Also, in some cases, they can enhance the reactivity of chemical reagents. In this review, we aimed at showing the synthesis of different organophosphorus compounds under green and mild conditions using ILs as reaction media or catalysts, according to a trend developed in the last years. A novel trend is to perform these syntheses under microwave irradiation conditions together with ILs as solvents and catalysts.