Use of magnesium implants is a new trend in orthopedic research because it has several important properties that recommend it as an excellent resorbable biomaterial for implants. In this study, the corrosion rate and behavior of magnesium alloys during the biodegradation process were determined by in vitro assays, evolution of hydrogen release, and weight loss, and further by in vivo assays (implantation in rabbits’ bone and muscle tissue). In these tests, we also used imaging assessments and histological examination of different tissue types near explants. In our study, we analyzed the Mg-1Ca alloy and all the hypotheses regarding the toxic effects found in in vitro studies from the literature and those from this in vitro study were rejected by the data obtained by the in vivo study. Thus, the Mg-1Ca alloy represents a promising solution for orthopedic surgery at the present time, being able to find applicability in the small bones: hand or foot.

Trauma orthopaedic surgery was the first domain to use degradable metallic implants made of magnesium alloys since the early 20th century. Unfortunately, the major limitation that consists of rapid degradation and subsequent implant failure, which occur in physiological environments with a pH between 7.4 and 7.6, prevents its widespread application. The biggest challenge in corrosion assay is the choice of the testing medium in order to reproduce more closely in vivo conditions. The current study was focused on two Mg-Zn-Ag alloys (Mg7Zn1Ag and Mg6Zn3Ag) and the Mg1Ca alloy. Dulbecco’s Modified Eagle Medium (DMEM) and Kokubo’s simulated body fluid solution (SBF) were selected as testing mediums and we follow the corrosion evaluation by the corrosion rate and mass loss. Also, the corrosion behaviour was interpreted in correlation with the microstructural features and alloying elements of the experimental magnesium-based alloys revealed by optical microscopy (OM), X-ray diffraction (XRD), and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDX). The experimental results highlight the more corrosive nature of the SBF environment and that a higher percentage of silver (2.5 wt.%) exhibited a better corrosion resistance. We consider that the magnesium alloy Mg6Zn3Ag showed valuable biodegradation characteristics to be considered as raw materials for manufacturing small trauma implants.