The use of electronic devices that incorporate multilayer ceramic capacitors (MLCCs) is on the rise, requiring materials with good electrical properties and a narrow band gap. This study synthesized yttrium-substituted barium titanate (Ba_1-x Y _x TiO₃, BYT) using a sol-gel process at 950 °C with varying concentrations of yttrium (0 ≤ x ≤ 0.3). X-ray diffraction analysis showed that the tetragonal phase became less pronounced as the yttrium content increased. The samples had varying grain sizes and porosity, with the BY30%T sample having the narrowest band gap at 2.21 eV. The BYT ceramic with 30% yttrium had a thermal conductivity of up to 7 W/m K and an electrical conductivity down to 0.002 (Ω cm)^-1 at 180 °C. The current-voltage characteristics of the BYT MLCC were also studied, showing potential use in next-generation high-capacity MLCCs. This work presents BYT as a promising material for these types of capacitors.

To study the structural, electronic, and optical properties of lead-free Barium titanate BaTiO₃ (BT) ferroelectric material in its tetragonal structure, a combination of experimental and theoretical studies has been used and the obtained results were discussed. The studied BT compound was prepared via the sol–gel technique. The calculated bandgap energy (E_g) and structural parameters of BT are determined using four types of exchange–correlation functionals (PBE, PBEsol, LDA, and PW91) in the perspective of the density functional theory (DFT). XRD and Raman analysis have shown that BT ceramic exhibits a tetragonal phase structure without any trace of impurity phases. The UV–vis investigation showed that BT has a bandgap energy of 3.19 eV, which is larger than the theoretically calculated values. The computed lattice parameter c is overestimated (as large as ~1% deviation) when using the LDA approximation. In contrast, PBEsol proved that those lattice constants were close to the experimental values (a deviation of less than 1%).

The BTO, BFTC, and BCTF compounds were synthesized by the sol-gel method. The XRD study revealed the formation of single-phase tetragonal perovskite structures with the space group (P4mm). The crystalline parameters were studied as a function of Fe and Co contents and occupation of Ba and/or Ti sites by Fe and Co in the BTO lattice. It was found that the obtained strain increases when Ba²⁺ is substituted by Co²⁺ and Ti⁴⁺ by Fe³⁺. The Raman investigation confirmed the existence of three active modes (B1/E (TO1LO), (E (TO)/A1(TO3), and (A 1(LO)/E (TO), all of which are related to the existence of the tetragonal phase and strongly support the XRD results. The microstructural study showed a clear correlation between the presence of Fe and Co and the grain size distribution. Optical studies revealed the improvement in band gap energy with transition-metal (Fe and Co) co-doped BTO ceramics. The decrease in the band gap is explained by the competing effects of Columbian interactions, microdeformation, and oxygen defects. The results indicate that the presence of Fe and Co dopants enhances the absorption in the BTO ceramic. The dopants demonstrated an effect on thermal conductivity: they decreased the thermal conductivity of BTO, which is in the range of 0.76-2.23 W m^-1 K^-1 at room temperature and 2.02-0.27 W m^-1 K^-1 at elevated temperatures. The microstructure of the manufactured materials and the grain size distribution affect the compressive strength.

In this study, we prepared a homogeneous fine powder of barium titanate (BaTiO₃, BT) doped with different concentrations of strontium (x = 0, 0.05, 0.125, 0.15, 0.20, and 0.3) and having the composition Ba_1-xSr_xTiO₃ (barium strontium titanate, BSr_xT). XRD patterns and Rietveld refinement revealed the existence of a single tetragonal phase structure for BSrxT, x = 0–20%, and a single cubic structure for BSr30%T. The physical properties of the pure and doped mixtures were studied. The results showed that the addition of strontium to the physical properties of BaTiO_3, including the apparent porosity, bulk density, linear shrinkage, and water absorption have been changed when increasing the Sr content. Moreover, the inclusion of 15% Sr in BaTiO₃ increases the apparent porosity and water absorption of the sample to 6.2 and 28.5%, respectively. The optical properties were investigated by Ultraviolet–visible spectroscopy and it was found that the optical band gap decreases significantly with increasing Sr concentration, from 3.10 for pure BaTiO₃ to 2.46 eV for the BSr30%T compound. The thermal conductivity measurements showed that the doping mechanism and the increased temperature have a significant effect on the thermal conductivity results of the fabricated ceramic materials. Therefore, it was found that the value of thermal conductivity increases with increasing Sr doping and at higher temperatures. A correlated behavior of optimum values is observed in band gap energy, absorption, and thermal conductivity which can be exploited for thermo-optical applications.