Graphite carbon nitride (g-C₃N₄) is a low band gap non-metallic polymer semiconductor that has broad application prospects and is an ideal material for absorbing visible light, as g-C₃N₄ materials have strong oxidation properties and are easy to modify. The structure formation of g-C₃N₄-based materials makes a series of photocatalytic synthesis reactions possible and improves photocatalytic reaction activity. In this paper, the development history, structures, and performance of g-C₃N₄ are briefly introduced, and the modification strategies of g-C₃N₄ are summarized to improve its photocatalytic and photoelectric catalytic properties via doping, heterojunction construction, etc. The light absorption and utilization of the catalysts are also analyzed in terms of light source conditions, and the application of g-C₃N₄ and its modified materials in photocatalysis and photocatalytic degradation is reviewed.

While vanadium-extracted tailings contain valuable components, their utilization is difficult due to their high sodium content. In this work, a new oxygen-pressure calcification and alkaline leaching strategy to achieve barium orthovanadate vanadium precipitation is developed to realize the resourceful recycling and utilization of vanadium-extracted tailings. First, the preparation of barium orthovanadate via calcified alkaline leaching and vanadium precipitation was studied, and the effects of CaO addition, NaOH concentration, leaching temperature, and liquid–solid ratio on the leaching rates of sodium and vanadium were evaluated in single-factor experiments. Under the optimum leaching conditions (CaO addition of 20%, alkali concentration of 150 g·L⁻¹, leaching temperature of 180 °C, and liquid–solid ratio of 10:1), the leaching rates of vanadium and sodium reached 85.25% and 82.36%, respectively. Subsequently, the vanadium-containing leaching solution was subjected to a vanadium precipitation test, and the effects of pH, Ba(OH)₂ addition (expressed as ${\mathrm{n}}_{\mathrm{Ba}}/{\mathrm{n}}_{\mathrm{V}}$), vanadium precipitation temperature, and vanadium precipitation time on the vanadium precipitation rate were investigated. Under the optimum vanadium precipitation conditions (pH 14, ${\mathrm{n}}_{\mathrm{Ba}}/{\mathrm{n}}_{\mathrm{V}}$ = 1.5:1, temperature of 30 °C, reaction time of 60 min), a vanadium precipitation rate of more than 99% was achieved. The precipitated vanadium product of this reaction was confirmed to be Ba₃(VO₄)₂ with a purity of more than 99%. Notably, the wastewater generated during the test process can be mixed with an alkali and returned to the leaching process for reuse, and the dealkalized residue can be used as a raw material for ore reduction in iron smelting processes.

CuO/TiO₂ is a highly active visible-light-driven photocatalyst. The precise structural regulation of TiO₂ and the quantum dot-scale loading strategy of CuO have long been researching hotspots and challenges. This work presents an ingenious synthetic strategy, leveraging the photoinduced superhydrophilicity and dark-induced reversible hydrophobicity of TiO₂, coupled with carbon quantum dots (CQDs) as “seeds” to induce the in situ synthesis of CuO quantum dots (CuO QDs). Specifically, CuO QDs with an average diameter of 5–10 nm were successfully anchored onto TiO₂ nanowire arrays (TNWAs) with a diameter of 10–15 nm. By adjusting the dosage of “seeds” (CQDs), the loading amount of CuO QDs can be effectively controlled. Corresponding characterizations were performed, including ultraviolet-visible-near-infrared (UV-Vis-NIR spectroscopy) for optical absorption properties, photoluminescence (PL) spectroscopy for photoluminescent behavior, electron paramagnetic resonance (EPR) spectroscopy for free radical generation capability, and bisphenol A (BPA) degradation assays for photocatalytic performance. Loading 4.78 wt% CuO QDs can effectively inhibit the recombination of electron–hole pairs in TNWAs. Simultaneously, it prolongs the lifetime of charge carriers (photoelectrons) and enhances the yields of hydroxyl radicals (•OH) and superoxide radicals (•O₂⁻). The BPA degradation efficiency of the CuO QDs/TNWA composite is 2.4 times higher than that of TNWAs. Furthermore, we found that the loading of CuO QDs significantly modulates the depletion layer width of the P–N heterojunction, and the underlying mechanism has been discussed in detail.