This work discusses the applicability of polyaniline-modified cation exchange membranes for the separation of monovalent/divalent cations by electrodialysis. A novel method of membrane modification directly in the electrodialysis unit is used to prepare permselective membranes. Complex characterization of the membranes before and after modification allows revealing the influence of membrane matrix on the modification efficiency. The characterization of the membranes includes determination of the diffusion permeability, specific conductivity and current–voltage curves in HCl, NaCl and CaCl₂ solutions, as well as transport-structural parameters of the extended three-wire model. The characterization results are used to predict the influence of the modification on membrane permselectivity. The competitive mass transfer of singly and doubly charged cations in the electrodialysis process is investigated in underlimiting and overlimiting currents. Electrodialysis desalination of a solution containing Na⁺/Ca²⁺ or H⁺/Ca²⁺ cations shows that the modification leads to an increase in membrane permselectivity to single-charged cations due to the repulsion of Ca²⁺ ions from the positively charged membrane surface. The permselectivity of the polyaniline-modified perfluorinated membrane to H⁺ in the mixture of H⁺/Ca²⁺ cations is observed in all current regimes.

Profiled ion-exchange membranes are promising for improving the parameters of reverse electrodialysis due to the reduction of pumping power and electrical resistance. The smooth commercial heterogeneous cation-exchange MK-40 and anion-exchange MA-41 membranes were chosen as the initial membranes. Profiled membranes with three different types of surface profiles were obtained by hot pressing the initial membranes. The bilayer membranes were made on the basis of single-layer profiled membranes by casting MF-4SK film on the profiled surfaces. The diffusion permeability of all types of single-layer and bilayer profiled membranes was higher than of the initial ones due to the appearance of large defects on their surface during pressing. The conductivity of the profiled membrane was lower in the diluted solution and higher in the concentrated solution than of the initial one for all samples except for the bilayer anion-exchange membrane. The conductivity of that sample was lower than that of the initial anion-exchange MA-41 membrane over the entire range of studied concentrations. The counter-ion transport numbers for all studied membranes were calculated based on the concentration dependences of conductivity and diffusion permeability of the membrane by the microheterogeneous model. The selectivity of single layer and bilayer profiled membranes became lower after their profiling due to the increase of the solution phases of membranes. The asymmetry of the current-voltage curves for all single-layer and bilayer profiled membranes was found. The application of the single layer and bilayer profiled membranes in reverse electrodialysis did not lead to an increase in power density.

A comprehensive study of the polyaniline influence on mineral scaling on the surface of the heterogeneous MK-40 sulfocationite membrane under electrodialysis has been conducted. Current-voltage curves and chronopotentiograms have been obtained and analyzed for the pristine MK-40 membrane and the MK-40 membrane which is surface-modified by polyaniline. The study of the electrochemical behavior of membranes has been accompanied by the simultaneous control of the pH of the solution outcoming from the desalination compartment. The mixture of Na₂CO₃, KCl, CaCl₂, and MgCl₂ is used as a model salt solution. Two limiting states are observed on the current-voltage curve of the surface-modified membrane. There is the first pseudo-limiting state in the range of small values of the potential drop. The second limiting current is comparable with that of the limiting current for the pristine membrane. It is shown that chronopotentiometry cannot be used as a self-sufficient method for membrane scaling identification on the surface-modified membrane at high currents. A mineral scale on the surfaces of the studied membranes has been found by scanning electron microscopy. The amount of precipitate is higher in the case of the surface-modified membrane compared with the pristine one.

The possibility of obtaining composite membranes based on MF-4SK and polyaniline with an anisotropic structure and asymmetric current-voltage curves in an external electric field was considered. The...