Magnesium alloy, as an absorbable and implantable biomaterial, has been greatly developed in the application field of biomaterials in recent years due to its excellent biocompatibility and biomechanics. However, due to the poor corrosion resistance of magnesium alloy in the physiological environment, the degradation rate will be unbalanced, which seriously affects the clinical use. There are two main ways to improve the corrosion resistance of magnesium alloy: one is by adding alloying elements, the other is by surface modification technology. Compared with adding alloy elements, the surface coating modification has the following advantages: (1) The surface coating modification is carried out without changing the matrix elements of magnesium alloy, avoiding the introduction of other elements; (2) The corrosion resistance of magnesium alloy can be improved by relatively simple physical, chemical, or electrochemical improvement. From the perspective of corrosion resistance and biocompatibility of biomedical magnesium alloy materials, this paper summarizes the application and characteristics of six different surface coating modifications in the biomedical magnesium alloy field, including chemical conversion method, micro-arc oxidation method, sol-gel method, electrophoretic deposition, hydrothermal method, and thermal spraying method. In the last section, it looks forward to the development prospect of surface coating modification and points out that preparing modified coatings on the implant surface combined with various modification post-treatment technologies is the main direction to improve biocompatibility and realize clinical functionalization.

The magnesium alloys Mg-0.5Mn-2Zn, Mg-1.0Mn-2Zn, and Mg-1.5Mn-2Zn (wt.%) with potential biomedical applications, synthesized by powder metallurgy, were investigated to evaluate the influence of manganese content on their microstructure, mechanical properties, and corrosion resistance. The results show that Mg-Mn-Zn alloys prepared by powder metallurgy reached the maximum compressive stress of 316 MPa and the maximum bending strength of 186 MPa, showing their good resistance to compression and bending, and meeting the mechanical properties required for the human bone plate. With an increase in manganese content, the corrosion resistance improved. In the polarization curve, the maximum positive shift of corrosion potential was 92 mV and the maximum decrease of corrosion current density was 10.2%. It was concluded that, of the alloys tested, Mg-1.0Mn-2.0Zn (wt.%) had the best overall performance, and its maximum compressive stress force and corrosion current density reached 232.42 MPa and 1.32 × 10⁻⁵ A·cm⁻², respectively, being more suitable for service in human body fluids.