The setting behavior of geopolymers is affected by the type of source materials, alkali activators, mix formulations, and curing conditions. Calcium hydroxide is known to be an effective additive to shorten the setting period of geopolymers. However, there is still room for improvement in the understanding of the effect of calcium hydroxide on the setting and phase evolution of geopolymers. In this study, the setting behavior and phase evolution of geopolymer containing calcium hydroxide were investigated by XRD analysis. The setting time of the geopolymer was inconsistently shortened as the amount of calcium hydroxide increased. A low calcium hydroxide dose of up to 2% of the total mix weight could contribute to the enhancement of compressive strength of geopolymers besides a fast-setting effect. The C-S-H gel is rapidly precipitated at the early stage of reaction in geopolymers containing high calcium hydroxide with some of the calcium hydroxide remaining intact. The ex-situ high-temperature XRD analysis and Rietveld refinement results revealed that geopolymer and C-S-H gel transformed into Si-rich nepheline and wollastonite, respectively. The wollastonite was also observed in heat-treated geopolymers with a low calcium hydroxide dose. It is believed that C-S-H gel can be precipitated along with geopolymers regardless of how much calcium hydroxide is added.

Superplasticizers (cement concrete water reducers) are applied to improve the flowability of calcium-rich, alkali-activated materials, with inconsistent results. However, superplasticizer applications are limited in metakaolin-based geopolymers. The possibility of using polycarboxylate superplasticizers and methyl isobutyl carbinol (MIBC) to ameliorate the flowability of metakaolin-based geopolymers was investigated. The ratio of metakaolin, fumed silica, NaOH or KOH, and water in geopolymers at a Na₂O or K₂O:Al₂O₃:SiO₂:H₂O ratio = 1:1:4:10 or 1:1:4:11 was maintained in the formulations. In this study, ether- or ester-based polycarboxylate superplasticizers did not improve the workability of fresh metakaolin-based Na-geopolymers. A low MIBC dose (0.5 wt.% of metakaolin) improved the flowability by 19% and additionally increased the 7-day compressive strength by 22% from 68 to 83 MPa for plain Na-geopolymers. The entrained fine froths produced by adding MIBC during mixing likely reduced friction between metakaolin particles, and the slurry became more workable. Hence, the geopolymer mixture with an improved flowability became more homogenous, which ensured more extensive metakaolin dissolution and hydrolysis. A low MIBC dose could be effective for Na-geopolymers with dual benefits of improved workability and enhanced compressive strength.