Phase change materials (PCMs) are an effective thermal mass and their integration into the structure of a building can reduce the ongoing costs of building operation, such as daily heating/cooling. PCMs as a thermal mass can absorb and retard heat loss to the building interior, maintaining comfort in the building. Although a large number of PCMs have been reported in the literature, only a handful of them, with their respective advantages and disadvantages, are suitable for building wall construction. Based on the information available in the literature, a critical evaluation of PCMs was performed in this paper, focusing on two aspects: (i) PCMs for building wall applications and (ii) the inclusion of PCMs in building wall applications. Four different PCMs, namely paraffin wax, fatty acids, hydrated salts, and butyl stearate, were identified as being the most suitable for building wall applications and these are explained in detail in terms of their physical and thermal properties. Although there are several PCM encapsulation techniques, the direct application of PCM in concrete admixtures is the most economical method to keep costs within manageable limits. However, care should be taken to ensure that PCM does not leak or drip from the building wall.

The building and construction sector has a huge impact on the environment because of the enormous amounts of natural resources and energy consumed during the life cycle of construction projects. In this study, we evaluated the potential environmental impact of the construction of a villa, from cradle to grave, in the Saudi Arabian context. Centrum voor Milieukunde Leiden (CML) for Centre of Environmental Science of Leiden University-IA baseline v3.03 methods were used to obtain the environmental profile for the impact categories, and Cumulative Energy Demand v1.09 was used to measure the embodied energy of the villa life cycle. The analyzed midpoint impact categories include global warming (GWP100a), ozone layer depletion (ODP), acidification (AP), eutrophication (EP), photochemical oxidation (POCP), and indicator cumulative energy demand (CED). The operation use phase of the villa was found to have the highest global warming potential and acidification with 2.61 × 10⁶ kg CO₂-eq and 1.75 × 10⁴ kg SO₂-eq, respectively. Sensitivity analysis was performed on the Saudi Arabian plans to increase the share of renewable sources and reduce the amount of electricity generated from hydrocarbons, which currently represents 46% of the total installed power, by 2032. The results showed that compared with the current electricity environmental impact, the CO₂ emission from electricity will decrease by 53%, which represents a significant reduction in environmental impact. The findings will help with the life cycle assessment of structures during future planning and for energy conservation.

The present work investigates the formation and microstructural and micro-mechanical characterization of the recast layer that formed on Inconel 718 alloy in the course of the wire electro-discharge machining (WEDM). The as-machined surface contains globules, shallow cracks, and re-deposition of molten materials, together with the elements from the decomposition of wire electrode and electrolyte, which does not exceed beyond the surface of the recast layer. Under presently investigated machining parameters, the recast layer was about 6.2 ± 2.1 µm thick. There was no presence of a heat-affected zone (HAZ), as otherwise indicated for other hard-to-cut materials. The transmission electron microscopy (TEM) and electron back-scattered diffraction (EBSD) investigations show that the microstructure of the recast layer is similar to that of bulk alloy. Micro-mechanical characterizations of the recast layer were investigated via in-situ micro-pillar compression on the micro-pillars fabricated on the recast layer. The strength of the superficial layer (1151.6 ± 51.1 MPa) was about 2.2 times higher than that of the base material (523.2 ± 22.1 MPa), as revealed by the in-situ micro-pillar compression.