Colloidal solutions of silver nanoparticles (AgNPs) were synthesized by gamma Co-60 irradiation using different stabilizers, namely polyvinyl pyrrolidone (PVP), polyvinyl alcohol (PVA), alginate, and sericin. The particle size measured from TEM images was 4.3, 6.1, 7.6, and 10.2 nm for AgNPs/PVP, AgNPs/PVA, AgNPs/alginate, and AgNPs/sericin, respectively. The influence of different stabilizers on the antibacterial activity of AgNPs was investigated. Results showed that AgNPs/alginate exhibited the highest antibacterial activity against Escherichia coli (E. coli) among the as-synthesized AgNPs. Handwash solution has been prepared using Na lauryl sulfate as surfactant, hydroxyethyl cellulose as binder, and 15 mg/L of AgNPs/alginate as antimicrobial agent. The obtained results on the antibacterial test of handwash for the dilution to 3 mg AgNPs/L showed that the antibacterial efficiency against E. coli was of 74.6%, 89.8%, and 99.0% for the contacted time of 1, 3, and 5 min, respectively. Thus, due to the biocompatibility of alginate extracted from seaweed and highly antimicrobial activity of AgNPs synthesized by gamma Co-60 irradiation, AgNPs/alginate is promising to use as an antimicrobial agent in biomedicine, cosmetic, and in other fields.

Cu nanoparticles are a potential material for creating novel alternative antimicrobial products due to their unique antibacterial/antifungal properties, stability, dispersion, low cost and abundance as well as being economical and ecofriendly. In this work, carboxymethyl cellulose coated core/shell SiO₂@Cu nanoparticles (NPs) were synthesized by a simple and effective chemical reduction process. The initial SiO₂ NPs, which were prepared from rice husk ash, were coated by a copper ultrathin film using hydrazine and carboxymethyl cellulose (CMC) as reducing agent and stable agent, respectively. The core/shell SiO₂@Cu nanoparticles with an average size of ~19 nm were surrounded by CMC. The results indicated that the SiO₂@Cu@CMC suspension was a homogenous morphology with a spherical shape, regular dispersion and good stability. Furthermore, the multicomponent SiO₂@Cu@CMC NPs showed good antifungal activity against Phytophthora capsici (P. capsici). The novel Cu NPs-based multicomponent suspension is a key compound in the development of new fungicides for the control of the Phytophthora disease.

In this study, the gamma ray-induced Maillard reaction method was carried out for chitosan (CTS) and glucosamine (GA) to improve the water solubility and antibacterial activity. The mixture solution of CTS and GA was exposed to gamma rays at a dose of 25 kGy and freeze-dried to obtain a Maillard reaction product (MRP) powder. The physicochemical and biological properties of the CTS-GA MRP powder were investigated. The CTS-GA MRP powder expressed good solubility at a concentration of 0.05 g/mL. In addition, the result of the antibacterial activity test against Escherichia coli revealed that the CTS-GA MRP powder exhibited highly antibacterial activity at pH 7; in particular, bacterial density was reduced by over 4 logs. Furthermore, the cytotoxicity test of the CTS-GA MRP powder on mouse fibroblast cells (L929) showed non-cytotoxicity with high cell viability (>90%) at concentrations of 0.1–1 mg/mL. Owing to the high antibacterial activity and low cytotoxicity, the water-soluble CTS-GA MRP powder can be used as a favorable natural preservative for food and cosmetics.