Metal sulfides for hydrogen evolution catalysis typically suffer from unfavorable hydrogen desorption properties due to the strong interaction between the adsorbed H and the intensely electronegative sulfur. Here, we demonstrate a general strategy to improve the hydrogen evolution catalysis of metal sulfides by modulating the surface electron densities. The N modulated NiCo₂S₄ nanowire arrays exhibit an overpotential of 41 mV at 10 mA cm⁻² and a Tafel slope of 37 mV dec⁻¹, which are very close to the performance of the benchmark Pt/C in alkaline condition. X-ray photoelectron spectroscopy, synchrotron-based X-ray absorption spectroscopy, and density functional theory studies consistently confirm the surface electron densities of NiCo₂S₄ have been effectively manipulated by N doping. The capability to modulate the electron densities of the catalytic sites could provide valuable insights for the rational design of highly efficient catalysts for hydrogen evolution and beyond.

Molybdenum disulfide is naturally inert for alkaline hydrogen evolution catalysis, due to its unfavorable water adsorption and dissociation feature originated from the unsuitable orbital orientation. Herein, we successfully endow molybdenum disulfide with exceptional alkaline hydrogen evolution capability by carbon-induced orbital modulation. The prepared carbon doped molybdenum disulfide displays an unprecedented overpotential of 45 mV at 10 mA cm⁻², which is substantially lower than 228 mV of the molybdenum disulfide and also represents the best alkaline hydrogen evolution catalytic activity among the ever-reported molybdenum disulfide catalysts. Fine structural analysis indicates the electronic and coordination structures of molybdenum disulfide have been significantly changed with carbon incorporation. Moreover, theoretical calculation further reveals carbon doping could create empty 2p orbitals perpendicular to the basal plane, enabling energetically favorable water adsorption and dissociation. The concept of orbital modulation could offer a unique approach for the rational design of hydrogen evolution catalysts and beyond.

P-rich transition metal phosphides (TMPs) with abundant P sites have been predicted to be more favorable for hydrogen evolution reaction (HER) catalysis. However, the actual activities of P-rich TMPs do not behave as expected, and the underlying essence especially at the atomic level is also ambiguous. Our structural analysis reveals the inferior activity could stem from the reduced overlap of atomic wave functions between metal and P with the increase in P contents, which consequently results in too strong P-H interaction. To this end, we used N-induced lattice contraction to generally boost the HER catalysis of P-rich TMPs including CoP₂, FeP₂, NiP₂, and MoP₂. Refined structural characterization and theoretical analysis indicate the N-P strong interaction could increase the atomic wave function overlap and eventually modulate the H adsorption strength. The concept of lattice engineering offers a new vision for tuning the catalytic activities of P-rich TMPs and beyond.