The effects of start and finish cooling temperatures on microstructure and mechanical properties of low-carbon high-strength and low-yield ratio bainitic steels were investigated in this study. Four kinds of low-carbon high-strength and low-yield ratio bainitic steels were fabricated by varying the start and finish cooling temperatures and cooling rates, and their microstructure and mechanical properties such as tensile and Charpy impact properties were measured. In the steels cooled down from the high start cooling temperature above Ar₁ [978 K (705 °C)], the volume fraction of acicular ferrite is lower than in the steels cooled down from the low start cooling temperature below Ar₁ [978 K (705 °C)]. The finish cooling temperatures and cooling rates affect the formation of bainitic ferrite, granular bainite, and martensite–austenite (MA) constituents. According to the correlation between microstructure and mechanical properties, the tensile strength increases with increasing the volume fractions of bainitic ferrite and MA constituents, whereas the elongation decreases. The yield ratio decreases as the volume fraction of MA constituents increases. Charpy impact absorbed energy is proportional to the volume fraction of acicular ferrite, and is inversely proportional to the volume fraction of granular bainite.

In this study, drop weight tear tests (DWTT) were conducted on API X70 and X80 linepipe steels fabricated with various compositions and rolling and cooling conditions in order to correlate the strain hardening with the abnormal cleavage fracture occurring in the hammer-impacted area. Area fractions of fracture modes were measured from fractured DWTT specimens, and the measured data were analyzed in relation to microstructures, Charpy impact energy, and strain hardening. All the steels consisted of fine acicular ferrite, together with some bainitic ferrite, granular bainite, and martensite-austenite constituent. As the volume fraction of acicular ferrite increased, the area fraction of DWTT abnormal cleavage fracture decreased because the toughness of acicular ferrite was higher than other microstructures. The area fraction of abnormal cleavage fracture was weakly related with strain hardening exponents obtained from the quasi-static tensile and compressive tests, but showed better correlation with those obtained from the dynamic compressive test. This tendency could be more clearly observed when steels having similar Charpy impact energy levels were grouped. Since the DWTT was performed under a dynamic loading condition, thus, the abnormal cleavage fracture behavior should be related with the strain hardening analyzed under a dynamic loading condition.