The bias-extension test is a rather simple experiment aiming to determine in-plane shear properties of textile composite reinforcements. However the mechanics during the test involves fibrous material at large shear strains and large rotations of the fibres. Several aspects are still being studied and are not yet modeled in a consensual manner. The standard analysis of the test is based on two assumptions: inextensibility of the fibers and rotations at the yarn crossovers without slippage. They lead to the development of zones with constant fibre orientations proper to the bias-extension test. Beyond the analysis of the test within these basic assumptions, the paper presents studies that have been carried out on the lack of verification of these hypothesis (slippage, tension in the yarns, effects of fibre bending). The effects of temperature, mesoscopic modeling and tension locking are also considered in the case of the bias-extension test.

Different approaches for the simulation of wrinkling during forming of textile reinforcements are presented. It is shown that 3D finite element modeling requires the consideration of an additional bending stiffness of the fibers. In shell-type modeling, the bending stiffness is important because it conditions the size of the wrinkles. Different methods to take into account the bending stiffness independently of the tensile stiffness are presented. The onset and development of wrinkles during forming is a global problem that concerns all deformation modes. It is shown in examples that the shear locking angle is not sufficient to conclude about the development of wrinkles. This article highlights the two points common to the different cases of wrinkling of continuous fiber textile reinforcements: the quasi-inextensibility of the fibers and the possible slippage between the fibers. It presents and compares different approaches to consider these two aspects. The simulation of the simultaneous forming of multilayered textile reinforcements makes it possible to see the influence of the orientation of different plies which is an important factor with regard to wrinkling.